摘要:CsPbX3(X = Cl,Br,I)钙钛矿量子点(QDs)作为一种热门的无机发光新材 料,由于其具有优异的光电性能和独特的结构特征,在发光二极管、太阳能电池、生 物医学以及公共安全等领域应用广泛。其中本文主要采用热注入法,通过控制其他反 应条件不变按不同比例的离子进行了五组实验,得到了五种化学性质稳定,发光强度 好的 CsPbX3(X = Cl,Br,I)钙钛矿量子点材料,进而形成对比,探讨反应离子比例 的不同对其光学性能和形貌特征,色纯度的影响。66281
毕业论文关键词:量子点材料;钙钛矿量子点;热注入法;光学性能;离子比例
Preparation of CsPbBr3 Perovskite Structure Quantum Dots and Its Luminescent Properties
Abstract: CsPbX3 (X = Cl, Br, I) perovskite quantum dots (QDs) as a popular new inorganic luminescent new material, due to its excellent photoelectric properties and unique structural features, in light-emitting diodes, solar cells, biomedical As well as public safety and other fields widely used.In this paper, five kinds of experiments were carried out by controlling the other reaction conditions according to different proportions of ions. Five kinds of CsPbX3 (X = Cl, Br, I) And the influence of the different ion ratio on the optical properties, morphology and color purity were investigated.
Key Words: Quantum dots materials; Perovskite quantum dots; Heat injection method; Optical performance; Ion ratio
目录
摘要 i
Abstract ii
1 绪论 5
1.1 引言 5
1.2 CsPbBr3 钙钛矿结构量子点的结构及其发光机理 5
1.2.1 CsPbBr3 钙钛矿结构量子点的结构 5
1.3 量子点的合成方法 6
1.3.1 离子注入法 7
1.3.2 沉淀法 7
1.3.3 胶体化学法 7
1.3.4 实验方法的选择 7
1.4 CsPbBr3 钙钛矿结构量子点的应用 8
1.4.1 发光二极管及光电显示方面的应用 8
1.4.2 光电子学方面的应用 8
1.4.4 公共安全方面的应用 8
1.4.5 多色实验和诊断方面的应用 9
1.5 CsPbBr3 钙钛矿结构量子点的研究现状 9
1.6 本课题的研究内容及目的 10
2 实验部分 11
2.1 实验药品 11
2.2 实验设备 11
2.3 量子点制备 12
2.3.1 实验步骤 12
2.3.2 实验流程图 13
2.4 测试与表征 13
2.4.1 X 射线衍射测试 13
2.4.2 吸收光谱测试 13
2.4.3 发射光谱测试 14
2.4.4 透射电子显微镜形貌 14
3 结果与讨论 CsPbBr3钙钛矿结构量子点的制备及其发光性质的研究:http://www.youerw.com/cailiao/lunwen_74146.html