毕业设计说明书中文摘要本课题是研究一种新型吸油材料——超疏水、超亲油二氧化硅气凝胶的制备以及应用。我们首先用溶剂热法制备Fe3O4纳米粉末，以Fe3O4作为磁核。用TEOS（正硅酸四乙酯）、APS为硅源，MTMS（甲基三甲氧基硅烷）作为表面疏水改性剂，制备出了一种超疏水的气凝胶。通过对不同类型油污的多次吸收试验，可得出本研究方法所制得的二氧化硅气凝胶吸油强，化学稳定性好，气凝胶的机械性能良好。以Fe3O4作为磁核，可以通过磁铁进行回收再利用。在多次试验以后仍有很强的油污吸附性和疏水性。这表明，本产品在油污处理问题上有着十分广阔的应用前景。78768

毕业论文关键词 ：二氧化硅气凝胶、Fe3O4纳米粒子、磁核、吸附

毕业设计说明书外文摘要

Title  The Application and preparation of super hydrophobic and   super oleophilic silica aerogel               

Abstract The project is study the application and preparation of super-hydrophobic andsuper oleophilic silica aerogel 。Firstly ,we make Fe3O4 nano particle as magneticnuclei by solvothermal method。 Preparing super-hydrophobic silica aerogel byusing TEOS, APS, MTMS。 Based on the different types of oil absorption test manytimes, we can concluded that the silica aerogel have high oil absorption ， good chemical stability，and good mechanical property。 Using Fe3O4 as magneticnuclei, we can recycle the silica aerogel by its magnetism。 After many experimentsthe silica aerogel still have strong oil adsorption and hydrophobicity。 The showsthat the product on the oil has a very broad application prospects。

Keywords  silica aerogel, Fe3O4 nano particle, magnetic nuclei, absorption

目  次

1 引言 1

1。1 研究背景 1

1。2海洋石油污染原因以及危害 1

1。2。1海洋石油污染的原因 1

1。2。2石油烃类在海水中存在方式 2

1。2。3海洋石油污染的危害 2

1。3 当前海洋石油污染的处理方法 3

1。3。1物理回收法 3

1。3。2化学处理法 5

1。3。3 生物降解法 6

1。3。4 处理方法总结 6

1。4 二氧化硅气凝胶 6

2 二氧化硅气凝胶的制备 8

2。1 Fe3O4纳米颗粒的制备方法介绍 8

2。1。1沉淀法 8

2。1。2 溶胶凝胶法 9

2。1。3 水热法 9

2。1。4 微乳液法 9

2。1。5溶剂热法 9

2。2 纳米Fe3O4制备 10

2。3 制备二氧化硅气凝胶 11

3 实验结果的测试与表征 12

3。1 Fe3O4纳米颗粒表征 12

3。1。1实验仪器 12

3。1。2 实验测试及表征 13

3。1。3 总结 15

3。2二氧化硅气凝胶测试及表征 超疏水超亲油的二氧化硅气凝胶的制备以及应用:http://www.youerw.com/cailiao/lunwen_90857.html