烯丙基聚氧乙烯醚基马来酸酐共聚物超塑化剂的制备

摘要本课题以烯丙基聚氧乙烯醚（APEG）为大单体、马来酸酐、丙烯酸等为主要原料，采用过硫酸铵（APS）为引发剂，通过溶液聚合反应，制备烯丙基聚氧乙烯醚-马来酸酐共聚物超塑化剂。通过改变马来酸酐与大单体APEG的摩尔比，丙烯酸与大单体APEG的摩尔比，甲基丙烯磺酸钠（MAS）与大单体的摩尔比以及反应时间，反应温度等条件，研究这些因素对聚羧酸超塑化剂的影响。通过测定水泥的净浆流动度确定最佳的制备聚羧酸系超塑化剂配方。通过SEM对水泥的微观结构进行分析。83366

试验结果表明，当 n(APEG):n(MA):n(MAS):n(丙烯酸)=1:3。5:0。26:0。77，引发剂

（APS）的用量为单体总质量的 1。36%，控制引发温度为 85℃，保温 2。5 个小时，制得的聚羧酸超塑化剂对水泥的净浆流动度最好达到 200mm。扫描电镜结果显示，与空白样品相比，加入聚羧酸系超塑化剂能够使水泥样块的孔径更加细化和均匀；养护 3 天与养护 10 天的样品相比养护 10 天后水泥块空隙明显比养护 3 天的小，水泥块的致密性也有所提高。

毕业论文关键词：超塑化剂；马来酸酐；净浆流动度；溶液聚合

Abstract In this topic, allyl polyoxyethylene ether (APEG) is monomer, maleic anhydride, acrylic acid is main raw materials,and the ammonium persulfate (APS) is using as initiator, the preparation of allyl polyoxyethylene ether - maleic anhydride copolymer super plasticizer is prepared through solution polymerization reaction。 The influence of reaction factors on preparing poly (carboxylic acid super plasticizer has been studied, such as the molar ratio of maleic anhydride and big monomer APEG, the molar ratio of acrylic acid and large monomer APEG, methyl allyl sulfonate (MAS) and large monomer mole ratio as well as the reaction time, and the reaction temperature。 The optimal formula of preparing poly carboxylic acid series super plasticizer was determine via the net cement paste fluidity measurent。 The microstructure of cement was analyzed through the SEM。

As a result, when n (APEG) : n (MA) : n (MAS) : n (acrylic acid) = 1:3。 5-0。 26:0。 77, the amount of initiator (APS) was 1。36% of the monomers total quality, and the temperature is controlled to 85 ℃, keeping 2。5 hours, the poly carboxylic acid super plasticizer on flowability of neat cement degree is best, up to 200 mm。Scanning electron microscopy (sem) results showed that, compared with the blank sample, adding poly carboxylic acid series super plasticizer can make cement specimens aperture more refinement and uniform; the curing concrete gap of sample which has maintenance for 10 days is of significantly smaller than the 3 days - maintenance sample, the density of concrete is improved。

Keywords: super plasticizer; maleic anhydride; flowability net; solution polymerization

第一章绪论 1

1。1 超塑化剂的概述 1

1。1。1 超塑化剂的涵义 1

1。1。2 超塑化剂的发展阶段及分类 1

1。1。3 超塑化剂的特点 3

1。2 超塑化剂的作用机理 3

1。3 超塑化剂的研究现状、存在问题及发展趋势 5

1。3。1 我国超塑化剂的研究现状 5

1。3。2 国外超塑化剂的研究情况 6

1。3。3 我国超塑化剂现存的问题 6

1。3。4 我国超塑化剂的市场现状和发展前景 7

1。4 超塑化剂的制备方法烯丙基聚氧乙烯醚基马来酸酐共聚物超塑化剂的制备:http://www.youerw.com/cailiao/lunwen_98256.html