摘要: 本文采用一种新的方法制备K2SiF6: Mn4+，制备过程中选用了常见的一些试剂: 高锰酸钾，二氧化硅，氢氟酸，油酸，乙醇和氢氧化钾等。在固定SiO2/KMnO4的摩尔比的情况下，主要研究分析表面活性剂OA油酸体积对其形貌和发光性能的影响。对所制备的样品进行发光性能检测，以此获得有关样品的微观结构、颗粒形貌及发光性能的影响研究。84766

毕业论文关键词: 表面活性剂；颗粒形貌；发光性能

Effect of Oleic acid on the Morphology and Luminescence Properties of K2SiF6: Mn4+

Abstract: A novel approach to the preparation of K2SiF6: Mn4+ was adopted in this paper and we chose certain reagents, such as potassium permanganate, silicon dioxide, hydrofluoric acid, oleic acid, ethanol and potassium hydroxide, etc。 In a fixed condition of the mole ratio of SiO2/KMnO4, the effects of the volumes of surfactant OA on the morphology and luminescence properties were mainly studied。 Performance testing for the prepared samples were also conducted, obtaining the influences on the samples' microstructure, particle morphology and luminescence properties。 

Key Words: Surface active agent; Particle morphology; Luminescence properties 

目    录

摘  要 1

引  言 1

1实验部分 2

1。1 仪器与试剂 2

1。2 化合物K2SiF6: Mn4+的合成 3

2样品的表征及性能测试 6

2。1 K2SiF6: Mn4+荧光粉晶体结构和形貌分析 6

3结  论 10

参考文献 11

致  谢 13

油酸对K2SiF6: Mn4+形貌及发光性能影响研究 

引言

科学家们合成出发光二极管，是本世纪最伟大的发明之一，它主要是由二氧化硅半导体材料的制成的，它是一种无污染的固体发光材料[1,3]。它有很多很多优点，它占据的空间面积较小；在能源危机问题提上日程以来，消耗的能源很低；它的传导时间很快，要比许多金属还要快很多[4,5]；而且它的稳定性较好，可以使用很长时间[6]；不会对环境造成破坏，这也是它的最大的优点之一[7,8]。为了解决它在应中的一些缺点，我们在二极管中加入了一些K2SiF6: Mn4+类的材料，从而完美的弥补了它的缺点[9]。论文网

    独特的电子、光学、磁以及催化性能使纳米技术被公认为是21世纪新兴技术的前沿[10,11]，我们通过充分的调节纳米材料微观结构的形貌，使我们对结构与性质的关系有了深入了解，才可以近一步的达到不仅能搞清研究还能充分的应用它[12]。K2SiF6:Mn4+是近两年才被发现的一类荧光粉,研究表明它在大约460 nm蓝光激发的过程中，会产生出高波数（大约600-700 nm）的红光，这一重要的研究结果表明，它可以应用在白光发光二极管中，这就增加了这方面研究的重要性，而且可以解决市场上此类材料的需求问题 [13]。从事材料科研的工作者们都会知道，晶体形貌对发光材料有多么重要的影响，如此微小的晶体形貌的改变，都会使得材料的性能产生天翻地覆的变化。而人们也一直采用各种方法在制备或分散纳米粒子的过程中对其进行表面修饰，以便改善纳米颗粒的形貌并减少其表面猝灭效应，以求获得优异的光学特性，进而提高其发光效率[14,15]。在我们的此次工作中，我们不得不用到表面活性剂，最重要的原因是，它的结构两端不仅具有亲水基团，还具有亲油基团，能够利用其长分子链的位阻效应可以防止纳米颗粒之间的聚集[16,17]。文献综述 油酸对K2SiF6:Mn4+形貌及发光性能影响研究:http://www.youerw.com/huaxue/lunwen_100817.html