摘 要：当今社会随着经济快速发展，带来了一系列副产物。其中水体污染尤为瞩目。如何既经济而又有效的去除水体中污染物，成为世界性问题。根据研究表明，吸附法是去除水中重金属离子最为有效的手法之一。本论文合成了希夫碱改性sba-15有序介孔材料，并利用射线衍射（XRD）、透射电镜（TEM）对SBA-15进行表征。结果表明，通过水杨醛功能化的SBA-15，在pH值等于5时，吸附剂用量为50mg时，对镍离子吸附处理最好。而随着温度的增加，镍离子的吸附率呈先增加再降低的趋势，在25℃时，共缩聚法改性的SBA-15的去除率最高；在23。5℃时，后嫁接法的SBA-15的去除率最高。通过研究，为近年来重金属离子造成水体污染后难以恢复的问题提供理论依据。93173
Abstract：Nowadays, with the rapid development of economy, it brings a series of by problems。Which is particularly concerned about water pollution。How to effectively solve pollutants in water is a worldwide problem。The SBA-15 was characterized by using X-ray diffraction(XRD) and transmission electron microscopy (TEM)。The results showed that the modified SBA-15, which was obtained by post grafting method, had the best adsorption to heavy metal ions at pH value of 5。The increase of the reaction temperature and increase the amount of adsorbent can make the adsorption rate increase; reaction temperature increased, the adsorption capacity of the adsorbent increases, and the increase of adsorbent dosage, it will lead to the adsorption capacity decreased。
keyword: SBA-15,chemical modification, Ni2+adsorption
目 录
1 绪论 5
1。1 水体重金属离子污染现状 5
1。1。1 水体重金属离子污染来源及危害 5
1。1。2 水体重金属污染的处理方法 6
1。2 介孔吸附剂在废水中的应用 6
1。2。1 介孔材料简介 6
1。2。2 废水中重金属离子的去除原理 7
2 实验部分 7
2。1试剂和药品 7
2。2实验仪器 8
2。3实验方法 8
2。3。1材料的合成 9
2。3。2材料的吸附性能的研究 9
3结果与讨论 10
3。1 XRD分析 10
3。2 N2吸附/脱附等温线 12
3。3TEM 分析 13
3。4改性材料对镍离子的吸附 14
3。4。1 pH对镍离子吸附的影响 14
3。4。2 吸附剂用量对镍离子的吸附影响 15
3。4。3 温度对镍离子的吸附影响 15
结论 17
参考文献 18
致谢 19
1。绪论来自优O尔P论R文T网WWw.YoueRw.com 加QQ7520`18766
介孔材料是孔径介于大孔和微孔之间的多孔材料，具有规则的孔道结构，对于废水中的重金属离子有很好的吸附作用[1,2,3]。水体重金属离子主要有铜、锌、铅、汞、六价铬、镉等[4]。 常见的重金属处理方法包括：化学沉淀法、离子交换法、氧化还原法、电解法以及吸附法等[5,6]。吸附法因其成本低、操作简单被广泛使用。[7] 希夫碱改性SBA-15有序介孔材料对NiⅡ吸附性能的研究:http://www.youerw.com/huaxue/lunwen_200978.html