摘要：以溶胶凝胶法和模板法所制备的La2Ti2O7粉体为前驱体，在氨气中氮化，制备出LaTiO2N粉体。采用X射线（XRD）、场发射扫描电子显微镜（SEM）对两种方法制备的前驱体及合成的金属氧氮化物进行表征，并且采用近红外反射性能测试、色度测试、耐酸碱度测试对合成的金属氧氮化物进行了测试。结果表明：XRD表征溶胶凝胶法和模板法均合成了活性较高的La2Ti2O7，粒径为35nm，950℃氮化后分别制备出了粒径为53nm的LaTiO2N和粒径为28nm的LaTiO2N。用SEM测试发现模板法制备LaTiO2N有明显蓝移，溶胶凝胶法制备的LaTiO2N有明显红移。两种方法制备出的LaTiO2N都有良好的色度和耐酸碱性。26706
关键词 金属氧氮化物 溶胶凝胶法 模板法 近红外反射
毕业论文设计说明书外文摘要
Title The synthesis of metal oxynitride nitride and infrared reflection performance research
Abstract
Lanthanum-titanate oxynitrides have been successfully prepared by ammonolysis of Metal Oxynitrides precursors resulting from sol-gel method and template method. The precursors and the resulting lanthanum-titanate oxynitrides were characterized by X-ray powder diffraction(XRD), scanning electron microscopy(SEM),and using near infrared reflectance performance testing, color testing, acid test for synthesis of oxynitride tested. The results showed that: sol-gel method and template method were synthesized higher activity Lanthanum-titanate oxynitrides, a particle size of 35nm,after 950℃ nitride prepared a diameter of 52nm of LaTiO2N. SEM test prepared by template method discovered precursor synthesized oxynitride significant blue shift, sol-gel method precursors synthesized oxynitride obvious red shift. Synthesis of the two methods oxynitride have good acid and alkali resistance.
Keywords Metal Oxynitrides sol-gel method template method Near infrared reflectance
目 录
1 绪论 1
1.1 引言 1
1.1.1 金属氧氮化物的研究进展 1
1.1.2 金属氧氮化物反射机理研究 2
1.1.3 金属氧氮化物合成影响因素分析 4
1.2 金属氧氮化物的应用领域 4
2 金属氧氮化物的制备 6
2.1 实验背景 6
2.2 实验试剂 6
2.3 实验仪器 7
2.4 实验测试方法 7
2.4.1 样品结晶性能的测定 7
2.4.2 扫描电镜测试 7
2.4.3 反射率测试 8
2.4.4 样品色彩性能测试 8
2.4.5 耐酸耐碱性测试 9
2.5 实验原理 9
2.6 实验部分 10
2.6.1 金属氧氮化物的制备 10
2.6.1.1 前驱体的制备 10
2.6.1.2 前驱体的氨解过程 12
2.6.2 金属氧氮化物的表征和分析 12
2.6.3 金属氧氮化物的性能检测 15
2.6.3.1 近红外反射性能检测 15
2.6.3.2 色彩性能检测 17
2.6.3.3 耐酸耐碱性的检测 18
2.7 实验结果与分析 19 金属氧氮化物LaTi（O,N）3纳米材料的制备及其红外反射性能研究:http://www.youerw.com/huaxue/lunwen_20969.html