摘要：氧化亚铜是一种及其重要的无机化工原料，在很多领域特别是在光催化领域有着非常广泛的应用。本次课题采用无机铜盐作为前驱体、采用不同的还原剂如甲酸或抗坏血酸等、通过氧化还原反应合成不同形貌的氧化亚铜纳米粒子；并进一步去研究其光催化性能。33074
毕业论文关键词：氧化亚铜；形貌；光催化
Study on the control of the morphology of cuprous oxide and its photocatalytic properties
Abstract：Cuprous oxide is a an important inorganic chemical raw materials in many fields and has a very wide range of applications in the field of photocatalysis especially. This topic used inorganic copper salt as precursor, using different reducing agents such as formic acid or ascorbic acid, synthesizing different morphology of cuprous oxide nanoparticles by oxidation reduction reaction synthesis, and further studying of its photocatalytic properties.
Key Words：Cuprous oxide;Morphology;Photocatalysis
目　录
1  绪论    3
1.1  引言    3
1.2  氧化亚铜的性质    4
1.3  纳米氧化亚铜的制备方法    5
1.3.1  化学沉淀法    5
1.3.2  水热法    5
1.3.3  溶剂热法    6
1.3.4  微乳液法    6
1.3.5  低温固相反应法    6
1.3.6  机械化学反应法    7
1.3.7  粉末冶金烧结法    7
1.3.8  电化学反应法    7
1.3.9  金属有机化合物的气相沉积技术(MOCVD)    8
1.3.10  声化学法    8
1.3.11  微波照射法    8
1.4  氧化亚铜的光催化性能    8
1.5  本课题的研究思路    9
2  实验部分    9
2.1 实验仪器及试剂    9
2.1.1  实验仪器    9
2.1.2  试剂及其物性常数    10
2.2  实验步奏    11
2.2.1  氧化亚铜的制备    11
2.2.2  氧化亚铜的表征    11
2.3  实验结果及讨论    14
2.3.1  氧化亚铜XRD分析结果    14
2.3.2  氧化亚铜SEM分析结果    15
2.3.3  氧化亚铜光催化性能分析结果    17
3  结论    21
致　谢    21
引用文献    22
 1  绪论
1.1  引言
纳米Cu2O的禁带宽度大约是2.0 eV，它是一种非常独特的p型金属氧化物半导体材料，在可见光区域的吸收系数比较高，能量转化率在理论上可达到12%，是合成太阳能电池的潜在材料，氧化亚铜(Cu2O)的应用前景表现在光电、信息功能、磁性材料和催化等许多方面。作为催化剂，Cu2O在石油化工和污水处理中有着广泛应用。Cu2O对许多气体具有敏感性，而且是一种非常有潜力的敏感材料。除此之外，Cu在地球上的含量丰富，同时Cu2O无毒且生产成本低。
光催化法能够非常好的除去环境的污染物(例如大气污染物、工业废水、饮用水和农业废水等等)，一般情况下，经过了一系列的反应，到最后能够达到全部矿化。但是利用太阳光处理污水的物质最常用的是TiO2，然而这种物质有诸多弊端，需要紫外活化，因此利用可见光作为光能来处理污水长期以来都是科学家们所追求的目标。在1998年，Ikeda等人证明了Cu2O在太阳光下可以具有很好的催化效果，而且第一次作出了用Cu2O作为催化剂在阳光下可以将水分解形成氢气和氧气是确实可行的结论。块状Cu2O量子效率比较低形成的，光生电子空穴对则较容易复合。当微粒从微米级变成纳米级时，复合率降低，可以提高量子效率。 氧化亚铜形貌控制及其光催化性能研究:http://www.youerw.com/huaxue/lunwen_29940.html