摘要:聚丙烯酸/聚异丙基丙烯酰胺互穿网络水凝胶的制备分为两步,第一步先制备出聚丙烯酸水凝胶,第二步与异丙基丙烯酰胺互穿,此方法被称之为分步法,接下来用溶胀率阐述了此互穿网络水凝胶在不同程度外部刺激下的反应情况,该外部刺激主要包括酸碱度,温度,从而明显的表现出了此水凝胶对酸性的敏感性能,另外,此互穿网络水凝胶对温度也表现出了相应的敏感的热缩性能。42923
毕业论文关键词:丙烯酸;聚异丙基丙烯酰胺;互穿网络水凝胶;温度敏感;酸碱度敏感;水凝胶
Preparation of Poly (Poly (Acrylic Acid) / Poly (ISO / Poly (Acrylic Acid) Hydrogel with Poly (Two)
Abstract: Poly (acrylic acid) / poly (N-isopropylacrylamide interpenetrating hydrogel network was pided into two steps, the first step to prepare poly (acrylic acid) hydrogels, the second step and N-isopropylacrylamide interpenetrating, this method is known as fractional step method, next with swelling rate describes the interpenetrating network hydrogel in different degree under external stimuli response to the situation, the external stimulation mainly include pH, temperature, which significantly the this hydrogel of acid sensitive performance. In addition, the interpenetrating network hydrogel on temperature also showed a corresponding sensitive heat shrinkable properties.
Key Words: Acrylic polymer; Poly acrylamide; Mutual gel; Temperature sensitive; pH sensitive; pH sensitive hydrogel
目 录
摘 要 1
引 言 1
1 实验部分 2
1.1 实验试剂和仪器 2
1.2 聚丙烯酸水凝胶制备 3
1.3 互穿网络水凝胶制备 3
1.4 互穿网络水凝胶溶胀率 3
1.5 互穿网络水凝胶的酸碱特性和温敏性 4
1.6 氯化钠的浓度对溶胀率的影响 4
1.7 互穿网络水凝胶的失水率 4
1.8 酸度值对失水率的影响 4
2 结果与讨论 4
2.1 互穿网络水凝胶溶胀的动力学 4
2.2 互穿网络水凝胶的酸度的敏感性 5
2.3 互穿网络水凝胶温度敏感行为 6
2.4 氯化钠的浓度对溶胀率的影响 7
2.5 互穿网络水凝胶失水动力学 8
3 结 论 10
参考文献 10
致 谢 12
聚丙烯酸/聚异丙基丙烯酰胺互穿网络水凝胶的制备(二)
引 言
水凝胶是由交联高分子网络包裹水所组成的一种非常特殊的分散体系,这种高分子网络发生的交联分为两种,分别为:化学交联,物理交联,其中水分子被这种交联高分子包含在其中而没有了流动性,水凝胶特别容易遭到损坏,而且是有弹性的,水凝胶的状态大可分为两种:固体,半固体。但是在以前,都把水凝胶认为是属于固体和液体的中间体,且能保持原有的形态。
几年来,人们越来越关注能够受外界的环境的影响,从而本身的溶胀性能发生相应的变化的水凝胶的探索和研究,这些外部环境分别为:酸碱度和温度。当这些水凝胶受到外部环境的影响时,它们的溶胀率会随着外部世界的不同而发生不同的变化,这些特别的性质能够使这些水凝胶在医学,各种物质的分离等方面都有非常大的应用。 聚丙烯酸/聚异丙基丙烯酰胺互穿网络水凝胶的制备:http://www.youerw.com/huaxue/lunwen_43561.html