摘要：金属有机骨架（MOFs，也称为配位聚合物，简述为配合物）是一类近年来开始广泛研究且具有良好应用前景的新型固体材料。它同时具备了无机和有机材料的性能。金属有机骨架材料具有大的比表面积、多孔性、空隙大和化学成分稳定等诸多性能，因此它具备了其它无机多孔材料所不能比拟的优势。本文主要研究了UiO-66-CN的另一条合成路线，从分子式出发先对其进行氰化，随后再次生成立体结构。同时制备了另一个催化剂Pd-MOF，并对其催化能力的测试以及在水介质中对于催化重氮盐产生C-C偶联反应的性能进行了温度、时间、催化剂量进行系统化的测试。62124

毕业论文关键词：金属有机骨架  催化剂  材料  合成  水介质

Design and synthesis of organic molecules skeleton MOF

Abstract: Metal Organic Frameworks（MOFs，namely coordination polymer）are a new type of solid material , which have an extensive application prospect that self-assemble with metal ions and organic ligands . While large surface areas, high microspores volumes ,good thermal stability and large windows are desirable for many applications .Heterogeneous catalysis is one of the earliest proposed applications for MOFs, as well as one of the earliest demonstrated applications. In this paper we focus on another synthetic route of UiO-66-CN, Its first departure from the formula cyanide, then generates a three-dimensional structure again. We also prepared another catalyst Pd-MOF and tested for its ability to catalyze, conducted a performance in an aqueous medium to produce the diazonium salt catalyzed C-C coupling reaction is carried out a systematic test temperature, time, amount of catalyst.

Key words: Metal Organic Frameworks  catalyst  solid material  synthesis  water  

1绪论 1

1.1研究背景及选题依据 1

1.1.1研究背景 1

1.1.2选题依据 1

1.2研究进程 2

1.3实验的主要研究内容 3

2.实验部分 4

2.1实验仪器与试剂 4

2.1.1实验试剂 4

2.1.2实验仪器 5

2.2实验内容 5

2.2.1 UiO-66-CN的合成 5

2.2.2 Pd-MOF的合成及性能研究 7

3.结果分析与讨论 9

3.1 2-溴-1，4-对二苯甲酸甲酯的合成 10

3.1.1反应机理 10

3.1.2结果与讨论 10

3.2 2-氰-1，4-对二苯甲酸甲酯的合成 11

3.2.1反应机理 11

3.2.2结果与讨论 11

3.3 2-氰-1，4对二苯甲酸的合成 11

3.3.1反应机理 11

3.3.2结果与讨论 11

3.4 UiO-66-CN的合成 12

3.4.1反应机理 13

3.4.2结果与讨论 13

3.5 Pd（C4H4N2O）2Cl2的合成 13

3.5.1反应机理 12

3.5.2结果与讨论 MOF有机分子骨架的设计与合成研究:http://www.youerw.com/huaxue/lunwen_68215.html