摘要:采用界面聚合法,聚乙烯醇在水的溶解下，加入到异佛尔酮二异氰酸酯和粉香香精的混合液中，在TMEDA催化剂下，制备出微胶囊香精。通过扫描电镜、滤镜、傅里叶红外光谱仪及热重分析仪分别对香精微胶囊的表面形貌、粒径分布、单体反应情况和热稳定性进行了分析表征。并分析了在不同浓度的聚乙烯醇和异佛尔酮二异氰酸酯下，其生成的微胶囊的形貌特征。结果表明，当聚乙烯醇采用1%的比例，异佛尔酮二异氰酸酯采用15%的比例，TMDEA采用2%的比例，其它因素不变的情况下，微胶囊形成最规则整齐的球形，反应得到的液体呈乳白色。71942
毕业论文关键词 聚脲； 聚乙烯醇 ；微胶囊； 异佛尔酮二异氰酸酯； 四甲基乙二胺
The preparation and process optimization of the aromatic essence which is slowly released by polyurea
Abstract: By interfacial polymerization, polyvinyl alcohol dissolve in water, to join the isophorone diisocyanate and powder compound mixture, under TMEDA catalysts, the preparation of microcapsule essence。 By scanning electron microscopy (sem), filters, Fourier infrared spectrometer and thermogravimetric analyzer, respectively, surface morphology, particle size distribution of subtle capsule, monomer reaction conditions and thermal stability are analyzed。 The morphological features of microcapsules were analyzed in different concentrations of polyvinyl alcohol and isofalone diisocyanate。 Results show that when the ratio of polyvinyl alcohol with 1%, isophorone diisocyanate by 15%, the proportion of TMDEA USES the proportion of 2%, other factors unchanged, under the condition of microcapsules form the rules of the spherical, the reaction liquid has milk-white。
Keywords: Polyurea ; PVA; Microcapsule； IPDI； TMEDA
目录
1引言 1
1。2 纳米胶囊香精的发展状况及其优缺点 1
1。3微胶囊技术简介 1
1。3。1微胶囊的囊材 2
1。3。2微胶囊的芯材 2
1。3。3 微胶囊化技术的应用 3
1。4香精胶囊化的方法 4
1。5本课题的研究目的和意义 6
2实验内容 7
2。1实验原料与仪器 7
2。1。1实验原料 7
2。1。2实验仪器 7
2。2实验原理 8
2。3香精微胶囊的工艺制备流程 9
2。3。1主要实验流程 9
2。3。2香精搅拌均质 10
2。3。3香精的微胶囊的包覆 10
2。3。4 微胶囊产品的处理 10
2。4香精微胶囊的表征 10
2。4。1粒径分布分析 10
2。4。2红外光谱分析 10
2。4。3形貌分析 11
2。4。4热重分析 11
2。4。5光学显微镜下的观察 11
3实验结果与讨论 12 以聚脲为壁材缓释香精的制备表征与工艺优化:http://www.youerw.com/huaxue/lunwen_81730.html