摘 要：本文通过表面接枝法将pH敏感性聚丙烯酸（PAA）接枝到凹凸棒石（ATP）表面，制备具有pH敏感性的PAA-g-ATP，并将其添加到聚偏氟乙烯（PVDF）铸膜液中，利用浸没沉淀法制备PVDF/PAA-g-ATP混合基质超滤膜。考察了铸膜液中改性凹凸棒石不同添加量对PVDF膜形貌、结构、纯水通量以及pH敏感性的影响。实验结果表明，PAA成功接枝在ATP表面。PAA-g-ATP的添加量对PVDF膜的孔径及孔隙率影响不大。改性凹凸棒石的添加量越大，其对应膜的纯水通量越大。纯PVDF膜的纯水通量几乎不随pH发生变化，而添加改性凹凸棒石的PVDF膜，其纯水通量则随pH的增大而减小。75918

毕业论文关键词：偏聚氟乙烯，凹凸棒石，pH敏感性，聚丙烯酸，表面接枝

Abstract: This research adopted the pH-sensitive PAA on the surface of ATP by surface grafting modification。 It added pH-sensitive modifier PAA-g-ATP into PVDF casting solution and fabricated hybrid ultrafiltration membrane of PVDF/PAA-g-ATP by immersion precipitation。 It studied the effects on morphology, structure, pure water flux and pH-sensitive of PVDF membrane, which are influenced by different modifier dosage。 Results showed that PAA could graft on ATP successfully。 The dosage of modifier has little influence on the pore size and porosity of PVDF membrane。 And the pure water flux of PVDF membrane changed larger with the more modifiers。 Finally, the pure water flux of pure PVDF membrane hardly changed by pH。 However, the PVDF membrane had added modifier have pure water flux decreased by the increasing pH。

Keywords：polyvinylidene fluoride, attapulgite, pH-sensitive, polyacrylic acid, surface grafting

目   录

1  绪论 3

1。1  膜的分类 3

1。2  偏聚氟乙烯膜的制备方法 4

1。3  偏聚氟乙烯膜的改性 5

1。4  pH敏感膜 6

1。5  本文的研究思路 6

2  实验部分 6

2。1  实验试剂和仪器 6

2。2  实验步骤 8

2。3  实验测试和分析方法 9

3  结果与讨论 11

3。1  PAA-g-ATP的表征 11

3。2  PVDF/PAA-g-ATP混合基质超滤膜的表征 13

3。3  PAA-g-ATP的含量对复合膜纯水通量的影响 20

3。4  PAA-g-ATP的含量对膜的pH敏感性分析 21

结  论 22

参 考 文 献 23

致  谢 26

1  绪论

1。1  膜的分类

1。1。1  按孔径大小分类

按膜的孔径大小分为：微滤膜、反渗透膜、超滤膜、纳滤膜等[1]（见表1-1）。

表1-1 按膜的孔径分类

分类 孔径范围 特点 类型

微滤膜 0。025-10 μm 膜孔整齐均匀、孔隙率高、膜厚度小等 多孔膜

反渗透膜 pH敏感聚偏氟乙烯/凹凸棒石混合基质超滤膜制备:http://www.youerw.com/huaxue/lunwen_86970.html