摘要本文选用苯乙烯（St）、丙烯酸（AA）为共聚单体，过氧化苯甲酰（BPO）为引发剂、异丙醇为溶剂、采用半连续溶液聚合工艺，合成分子量较小的苯丙树脂，采用H1-NMR、GPC等技术对苯丙树脂的结构进行分析。本文还考察了引发剂种类及数量、温度、单体比例等因素对苯丙树脂类高分子分散剂性能的影响。随着反应温度身高，分散体系的粘度减小，当丙烯酸：苯乙烯=6：4时，分散剂分散效果最好。76632
Abstract Through semi-continuous solution polymerization ,the selection of styrene (St), acrylic acid (AA) as monomer，benzoyl peroxide (BPO) as initiator, isopropyl alcohol as solvent, synthetic smaller molecular weight styrene acrylic。 The resin was characterized by H1-NMR 、GPC。 In this paper, the effects of initiator species, quantity, temperature, monomer ratio and other factors on the properties of styrene - acrylic polymer were also investigated。 With the reaction temperature rise,, the viscosity of the dispersion system decreases, when the acrylic acid: styrene =6:4, the dispersion effect is best。
毕业论文关键词：苯丙树脂； 高分子分散剂； 涂料； 分散稳定性
Keyword: Styrene-acrylic ；Polymer Dispersant; Coating；Dispersion Stability
目录
第一章 绪论 4
1。1引言 4
1。2分散剂概述 4
1。2。1分散剂的分类 4
1。2。2高分子分散剂的分类 5
1。2。3高分子分散剂的应用 5
1。3。1国内研究现状 6
1。3。2国外研究现状 6
1。4苯丙树脂的聚合方法 7
第二章 实验部分 7
2。1实验原料和试剂 7
2。2实验仪器及来源 8
2。3苯丙树脂的合成 8
2。3。1苯丙树脂合成的配方和工艺 8
2。3。2苯丙树脂的后处理 8
2。3。3树脂氨化方法 9
2。4分散性能的测试和分散剂沉降稳定性测试 9
2。5测试与表征 9
2。5。1核磁共振（H1-NMR） 9
2。5。2分子量及其分布的测定 9
2。5。3粘度和流变性能测试 10
2。5。4固含量和转化率的测定 10
第三章实验结果讨论 10
3。1核磁共振（H1-NMR） 10
3。2引发剂含量对聚合物分子量及其分布的影响 11
3。3温度对聚合反应的影响 12
3。4反应单体浓度对聚合反应的影响 13
3。5沉降稳定性的测定 13
第四章 结论 14
参考文献 15
致谢 17
第一章 绪论
1。1引言
传统涂料的组成主要为树脂和有机溶剂，然而有机溶剂容易挥发，在生产和使用过程中产生有毒的“三废”，对人类健康和生活造成负面影响。因此，环保型或者是“绿色”无污染型涂料的研究成为涂料行业未来发展的一个重要方向。环保型涂料以水性涂料为主，在生产过程中采用水作溶剂，具有生产使用过程安全、无毒、试剂价廉易得等众多优点。论文网 水性涂料分散剂的制备及性能研究:http://www.youerw.com/huaxue/lunwen_87929.html