摘要：纤维板因化学胶黏剂的使用，导致其对环境污染较为严重，研究绿色无污染的纤维板就成为了目前研究的热点。本论文主要研究漆酶对秸秆预处理的工艺，以期为绿色纤维板研制提供依据。首先对漆酶预处理工艺的单因子进行了优化，优化条件为：酶量30U/g，时间4h，固液比1:4，温度35℃；进一步进行了SAS响应面优化，优化结果为：酶量40U/g，反应时间3h，固液比1：4。67，pH4。5，反应温度30℃。在该条件下，研制的纤维板弯曲强度和弯曲弹性模量分别达到5。54MPa、40。30MPa，较未优化提高了1。56倍。该实验为漆酶处理制备力学性能优良的秸秆纤维自生胶合纤维板提供了理论依据。80047

毕业论文关键词：纤维板，漆酶，玉米秸秆，预处理，弯曲强度

Abstract:Environmental pollution is more serious because of the use of chemical adhesives of fiberboard,research on green non-pollution fiberboard has become a hotspot。This paper is the research on laccase treatment of straw, in order to provide the basis for development of green fiberboard 。 First process of the laccase treatment is optimized by single factor。 Optimum conditions:enzyme amount 30U/g,reaction time 4h,solid-to-liquid ratio 1:4, pH 4。5,treatment temperature 35℃; further for the SAS response surface optimization, optimization results: enzyme amount 40 U / g, reaction time 3h, solid-liquid ratio 1:4。67, pH4。5,treatment temperature 30℃。In this condition, the flexural strength and flexural modulus of fiber board are respectively reached 5。54MPa and 40。30MPa,with 1。56 times increase than before optimization。 。The research provided the theoretical guidance for production of self-bonding straw fiberboard with excellent performance。

Keywords:fiberboard, laccase, corn straw,pretreatment，flexural strength

目   录

1 前言 2

1。1 我国人造板现状 2

1。1。1 人造板中的甲醛污染 2

1。1。2 我国资源现状以及合理利用原料 3

1。2 无胶人造板的研究进展 3

1。2。1 无胶人造板的提出 3

1。2。2 国内外对无胶板的研究 3

1。2。3 木材成分分析 3

1。3 漆酶预处理生产无胶纤维板 4

1。4 研究思路 4

2 材料与方法 5

2。1 材料与仪器 5

2。1。1 秸秆 5

2。1。2 试剂 5

2。1。3 溶液 5

2。1。4 仪器设备 6

2。2 实验方案 6

2。2。1 漆酶预处理秸秆的单因素条件研究 6

2。2。2 纤维板响应面优化 8

2。2。3 纤维板热压方法 8

2。2。4 还原糖含量测定方法 9

2。2。5 力学强度测定 9

3 结果与分析 9

3。1 不同酶量对纤维板性能的影响 9

3。2 不同时间对纤维板性能的影响 11

3。3 不同固液比对纤维板性能的影响 (责任编辑：qin)