摘要聚乳酸是一种具有良好的生物可降解性、生物相容性的高分子材料[13]。本研究选用聚乳 酸（PLLA）/聚环氧乙烷（PEO）体系，溶液共混后通过刮膜这种简洁的方法成功制备了聚乳 酸多孔薄膜。研究发现：1、通过刮膜制备得到的 PLLA/PEO 薄膜，刻蚀 PEO 相可得到贯通的 PLLA 多孔薄膜。2、通过改变薄膜厚度进而实现对孔形貌的有效调控。3、制备得到的 PLLA 多孔薄膜拥有优秀的多孔性能；4、本论文中制备 PLLA 多孔薄膜的方法高效环保，有望推广 应用。88026

Polylactic acid is a kind of macromolecule material with good biodegradability and biocompatibility。 In this study, polylactic acid (PLLA) / polyethylene oxide (PEO) system was used, and the PLLA porous films were successfully prepared by scraping。 It is found that: 1。 The PLLA porous films can be obtained by etching the PEO phase of the PLLA/PEO films that were prepared by scraping。 2。 The mophology of porous structure would be changed with the thinkness of the films。 3。 The PLLA porous film has excellent porous performance。 4。 In this paper, the method of preparing PLLA porous films is highly effective and environmental, application prospects are very good。

毕业论文关键词：聚乳酸；刮膜；多孔结构

Keyword: Polylactic acid; Scraping; porous structure

1、前言 5

1。多孔材料定义 5

1。2 多孔材料类型 5

1。2。1 多孔金属材料 5

1。2。2 多孔陶瓷材料 6

1。2。3 泡沫塑料 7

1。2。4 多孔高分子材料 8

1。3 多孔材料的制备方法 10

1。4 聚乳酸的性质及特点 11

2．实验部分 12

2。1  实验原料 12

2。2  实验仪器、设备 12

2。3  样品制备 13

2。4  结构表征和测试 13

3。结果与分析 15

3。1 扫描电子显微镜（SEM） 15

3。2 抽滤实验 17

3。3 水通量分析 17源-于,优W尔Y论L文.网wwW.youeRw.com 原文+QQ75201,8766

3。3 动态光散射分析（DLS） 18

4。结论 19

参考文献 19

致谢 20

1、前言

1。1 多孔材料定义

多孔材料（Porous material）是一种由相互贯通的或封闭的孔洞构成网络结构材料， 孔洞的边界或表面是由支柱或平板构成[14]。孔的结构大致上可以分为三种：第一种是由于 形状类似于蜂房的六边形结构而被称为“蜂窝”材料；第二种是二维结构的孔，并且孔呈现

多边形的几何形态；第三种是由大量多面体形状的孔洞在空间上存在构成的三维结构。如果 构成孔洞的固体只存在于孔洞的边界处（即孔洞之间是相通的），就称为开孔；如果孔洞表 面也是实心的，即每个孔洞与周围孔洞完全隔开，相互独立，则称为闭孔；也有些孔洞是半 开孔半闭孔的。由于多孔材料具有相对密度低、比强度高、比表面积高、重量轻、隔音、隔 热、渗透性好等优点，其应用范围远远超过很多单一功能的材料，在航空、航天、化工、建 材、冶金、原子能、石化、机械、医药和环保等诸多领域具有广泛的应用前景[15]。