    摘要当今,国际功能材料等领域的一个研究热点就是多铁性材料的研究。由于多铁性材料具有磁电效应,所以在新型存储器、电子元件等方面有重要的应用价值。而在这方面,最具期望的室温多铁性材料之一的BiFeO3,在部分状态时表现出低的自发极化和饱和磁化强度值。这篇文章叙述了关于通过掺杂使BiFeO3室温多铁性增强的研究。25362
      本课题通过采用快速固相烧结法制备出BiFe1-xScxO3系列的陶瓷样品,并对其进行XRD结构分析、SEM形貌分析、介电性能分析和电滞回线分析。XRD结构分析发现较低浓度的Sc3+掺杂并不会改变其结构,但会使衍射峰左移因为Sc3+会使其晶胞增大。从SEM照片上看烧结温度为880℃时,样品的晶粒尺寸较大,致密度较好。介电性能分析表明介电常数会随着Sc掺杂浓度的提高而提高。通过铁电性能分析可以发现,Sc的掺杂浓度从0.03增加到0.05时,陶瓷的剩余极化率和矫顽电场都明显提高,分别从5.69μC/cm2增加到10.38μC/cm2,从1055Kv/cm增加到1269Kv/cm,BiFeO3的铁电性能提升。
    关键词  铁酸铋陶瓷  Sc掺杂  XRD 介电性能  电滞回线
    毕业论文设计说明书外文摘要
    Title    Research on the B-site doping of multiferroic materials                   
    Abstract
    At present,the research on multiferroic material is a rising area in the field of international functional material.The Magnetoelectric effect opens the new opportunities in magnetic recording, spintronics, etc. In this respect,BiFeO3 ,one of the most promising room temperature multiferroic material, exhibits a low spontaneous polarization and saturation magnetization values. The article gives an account of the research on the enhanced room temperature multiferroicity of BiFeO3 by using doping method .
    In this dissertation,BiFe1-xScxO3 ceramic samples were prepared by the fast solid-phase sintering.The XRD analysis revealed that the low concentration doping of  Sc did not change its structure, but diffraction peaks in the diffraction pattern shifted left slightly because doping Sc caused the cell increasing. SEM photographs confirmed 800℃ sintered grains were larger and performance were more excellent.Meanwhile,dielectric analysis showed that the dielectric constant were improved with the concentration of Sc doping getting higher. By analyzing ferroelectric properties,we reached a decision that when the concentration of Sc doping increased from 0.03 to 0.05, the residual polarization and coercive field of ceramics had increased significantly ,respectively from 5.69μC / cm2 to 10.38μC / cm2 and from 1055Kv / cm to 1269Kv / cm.Therefore,these results demonstrate
    that the multiderrocity could be enhanced by doping  Sc.
    Keywords  BiFeO3 ceramics,Sc-doped ,XRD,dielectric properties,ferroelectric hysteresis loop
    目   次
    1 引言    1
    2  多铁性基本概念     2
    2. 1铁磁性与铁电性    2 
    2. 2 多铁性简介    3
    3  多铁性材料BiFeO3简介    4
    3. 1 BiFeO3 结构    4
    3. 2 BiFeO3陶瓷的制备工艺     5
    3. 3 BiFeO3的研究现状     6
    4  本课题的研究内容和意义       7
    5   实验部分      8
    5. 1实验原料     8
    5. 2实验仪器    9
    5. 3实验方法    9
    5. 4 实验步骤    10
    6 实验结果与分析    11
    6. 1 XRD分析    13
    6. 2 SEM形貌分析    15
    6. 3介电性能测试    18
  1. 上一篇:高强铝合金多层结构钎焊过程变形与流场数值模拟
  2. 下一篇:Sr2FeMoO6/ZnO复合薄膜的制备及其磁性和输运研究
  1. 泡沫铝合金钎焊工艺性能研究

  2. 不同链长聚二甲基硅氧烷...

  3. 电弧离子镀TiAlN硬质薄膜的制备及性能研究

  4. 电弧离子镀TiCN硬质薄膜的制备及性能研究

  5. 高能微弧合金化沉积氮化...

  6. 稀土元素Dy对合金涂层结构与高温性能的影响

  7. 水性环氧树脂的制备及性能研究

  8. 江苏省某高中学生体质现状的调查研究

  9. 巴金《激流三部曲》高觉新的悲剧命运

  10. g-C3N4光催化剂的制备和光催化性能研究

  11. 上市公司股权结构对经营绩效的影响研究

  12. NFC协议物理层的软件实现+文献综述

  13. C++最短路径算法研究和程序设计

  14. 浅析中国古代宗法制度

  15. 现代简约美式风格在室内家装中的运用

  16. 中国传统元素在游戏角色...

  17. 高警觉工作人群的元情绪...

  

About

优尔论文网手机版...

主页:http://www.youerw.com

关闭返回