摘要：本文对聚氨酯弹性体进行了综述，包括聚氨酯基本概念、反应机理、制备
- 上一篇：燃烧合成制备YFeO3及其性能研究
- 下一篇：Pd-Cu-ClxAl2O3低温催化CO氧化的DFT研究
聚氨酯弹性体所需要的原料、以及聚氨酯弹性体的合成方法。以聚己二酸丁二醇
酯（PBA）、4，4′-二苯基甲烷二异氰酸酯（MDI）和二元醇1，4- 丁二醇（BDO）
为原料，采用一步法制备了热塑型聚氨酯弹性体，并使用傅立叶红外光谱仪和万
能试验机对材料进行了红外光谱和力学性能表征， 研究了二元醇作为扩链剂对聚
醚聚氨酯弹性体性能的影响。结果表明，在一定条件下，合成了聚氨酯弹性体，
随着BDO用量的增加，弹性体的冲击强度、拉伸强度、硬度性能提高，达到定
值后再增加用量反而使性能下降。3879
关键字：聚氨酯弹性体；扩链剂；性能
Study of the Synthesis of Polyurethane Materials
Abstract: Polyurethane, including the basic concept of polyurethane elastomer,
including reaction mechanism, the required raw materials, as well as the synthesis
methods of polyurethane elastomer, was summarized. Thermoplastic polyurethane
elastomer was prepared using one-step method with poly (butyl glycol ester of adipic
acid (PBA) and 4,4'- diphenylmethane diisocyanate (MDI) and glycol 1,4-butanediol
(BDO) as raw materials. The IR spectrum and mechanical properties of material were
characterized by the Fourier infrared spectrometer and universal testing machine. The
results show that, polyurethane elastomer was synthesized at a certain condition. With
an increasing in the amount of BDO, the impact strength, tensile-strength and
hardness increase. However, these properties of elastomer decrease after reaching
maximum value when more amount of BDO was added.
Key Words: Polyurethane elastomer；chain extender；Properties
目 录
1. 绪论 . 4
1.1 聚氨酯材料的分类 4
1.2 聚氨酯弹性体的概述 5
1.3 聚氨酯弹性体的分类 5
1.4 聚氨酯弹性体的优点 6
1.5 聚氨酯弹性体的应用 6
1.6 聚氨酯弹性体的未来发展趋势 7
1.7 课题研究目的意义与研究内容 8
2.实验 9
2.1 实验机理 . 9
2.2 合成方法 . 10
2.3 实验原料 10
2.4 实验药品及设备 16
2.5 实验步骤 16
2.6 性能测试 . 17
3.结果与讨论 21
3.1 聚氨酯弹性体合成研究 21
3.2 聚氨酯弹性体性能研究 23
3.3 应力-应变曲线 . 26
4．结论 . 28
致谢 . 29
参考文献 . 30，3879
1. 绪论
聚氨酯是聚氨基甲酸酯的简称，英文名称是 polyurethane，它是一种高分子
材料。聚氨酯是一种新兴的有机高分子材料，被誉为“第五大塑料” ，因其卓越
的性能而被广泛应用于国民经济众多领域。产品主要应用在轻工、化工、电子、
纺织、医疗、建筑、建材、汽车、国防、航天、航空等领域。
1.1 聚氨酯材料的分类
聚氨酯材料可用在国民生活的各个领域，应用范围非常广。下面列举出部分
具有一定代表性的产品作简要介绍。
（1） 聚氨酯泡沫材料：分为硬质聚氨酯泡沫、半硬质聚氨酯泡沫和软质聚氨
酯泡沫材料。硬质聚氨酯泡沫主要用于建筑隔热材料、保温材料（管道
设施等的保温隔热）、生活用品（床、沙发等的垫材、冰箱，空调等的隔