    摘要氮氧化物是最主要的大气污染物，我国的氮氧化物90%来自煤炭的直接燃烧产生的烟气。选择性催化还原法是目前最有效地脱除氮氧化物的方法。
    制备了不同F/Ti摩尔比(RF/Ti×100) (0, 0.5, 1, 1.35 和 2)的V2O5/TiO2催化剂用于氨法选择性催化还原氮氧化物。实验发现，氟掺杂的V2O5/TiO2催化剂的活性优于未掺杂改性的。
    通过XRD, Raman，BET, TEM, H2-TPR，NH3-TPD和EPR表征分析，考察氟掺杂对催化剂的物化性质的影响。结果显示，氟掺杂改善催化剂活性的原因归因于：抑制颗粒增大、抑制锐钛矿向金红石的转化、提高了钒物种的还原能力和氧空位的生成。8788
        用EPR方法对催化剂样品进行了研究，实验表明，氧气能吸附于氧空位上，形成超氧自由基O2-,O2-为活性氧物种，其吸附量及配位环境可与催化活性相关联。
    关键词  选择性催化还原；V2O5/TiO2；氟掺杂；超氧自由基
    毕业设计说明书（论文）外文摘要
    Title Investigation on selective catalytic reduction of NOX by V2O5/TiO2 and their electron spin resonance
    Abstract
    Nitrogen oxides (NOX) are one of the main pollutants in the atmosphere, and 90% of its emission in our country originates from flue gas due to direct coal combustion. Selective catalytic reduction (SCR), has been shown an effective post-treatment process to eliminate nitrogen oxides.
    V2O5/TiO2 catalysts were prepared in the presence of (NH4)2TiF6 with controlled fluorine to titanium molar ratios (RF/Ti×100) (0, 0.5, 1, 1.35 and 2) for selective catalytic reduction of NOX by NH3 (SCR process). It was found that the NOX conversion over F-doping V2O5/TiO2 was greatly improved compared with pure V2O5/TiO2.
    The effects of F-doping on the structure of the catalysts were systematically examined using XRD, Raman spectrum, BET, TEM, H2-TPR，NH3-TPD, XPS and EPR. These results showed that F ions were incorporated into TiO2 lattice. The presence of fluorine in the catalysts was confirmed using X-ray photoelectron spectroscopy (XPS). The high catalytic activity was ascribed to several beneficial effects produced by F-doping: preventing the grain growth, inhibiting the phase transformation from anatase to rutile, higher reducibility of dispersed vanadia species, creation of oxygen vacancies, and increase of active sites. It was interesting to point out that the catalytic activity of F-dopingV2O5/TiO2 was achieved by the creation of surface oxygen vacancies.
    By using electron paramagnetic resonance (EPR) method, the oxygen adsorbed on the catalysts has been investigated. The EPR results confirm that the oxygen adsorbed to the oxygen vacancies can form superoxide radicals (O2-). The species O2- is the catalytic active one. Its concentration correlates with the catalytic activity.
    Keywords:  selective catalytic reduction; V2O5/TiO2; F-doping; superoxide radicals
     目录
    1  绪论    1
    1.1  课题研究背景    1
    1.2  我国能源环境现状及目标    1
    1.3  NOX污染危害及现状    2
    1.4  煤炭燃烧时NOX生成机理及控制技术    4
    1.5  选择性催化还原SCR脱除NOX技术简介    8
    1.6  EPR简介    13
    1.7  本课题研究目的及内容    14
    2  实验部分    15
    2.1  主要试剂与仪器    15
    2.2  催化剂制备    16
    2.3  催化剂活性测定    16
    2.4  催化剂的表征方法综述    18
    3  催化剂表征结果讨论及分析    18
    3.1  XRD分析结果与讨论    18
    3.2  Raman分析结果与讨论    20
    3.3  SEM测试结果与分析    22
  1. 上一篇：水中邻苯二甲酸酯类污染物的检测方法的研究
  2. 下一篇：防外漏高包覆长玻纤增强聚丙烯的研究

  1. 六方氮化硼纳米片对聚偏氟乙烯结晶性能响

  2. DTA和SEM实验氟铝酸铯中温铝钎剂的研究

  3. WO3掺杂g-C3N4/TiO2复合涂层的...

  4. 三维氮掺杂石墨烯的合成与表征

  5. 掺杂二氧化碲晶体的生长与表征

  6. 稀土掺杂锂钙硅酸盐发光行为研究

  7. 中红外激光晶体用Tm掺杂...

  8. C++最短路径算法研究和程序设计

  9. 浅析中国古代宗法制度

  10. 中国传统元素在游戏角色...

  11. NFC协议物理层的软件实现+文献综述

  12. 上市公司股权结构对经营绩效的影响研究

  13. g-C3N4光催化剂的制备和光催化性能研究

  14. 巴金《激流三部曲》高觉新的悲剧命运

  15. 高警觉工作人群的元情绪...

  16. 江苏省某高中学生体质现状的调查研究

  17. 现代简约美式风格在室内家装中的运用

　　

About

优尔论文网手机版...

主页：http://www.youerw.com

关闭返回