摘要S355钢是一种低合金高强度钢，由于该系列钢种具有良好的综合力学性能与工艺性能而在工程上被广泛应用。S355钢经过锻压成型后力学性能不能达到源供应态的力学性能，低温冲击功偏低。使用球化退化和正火工艺对S355钢板进行热处理，以便细化晶粒，提高钢板的低温冲击功。通过金相组织的观察和数据分析，经过球化退化和正火热处理过的S355钢的组织比较均匀细小，低温冲击功都能达到要求，其中正火风冷的钢板的低温冲击功最高，综合性能最好。68198

毕业论文关键词：S355；球化退火；正火；低温冲击韧性   

毕业设计说明书（论文）外文摘要

Title    research on technics to improve low temperature impact toughness of S355

Abstract

S355 steel is low alloy high strength steel, and is widely used in engineering because of the series of steel has good mechanical properties and process performance. After forging forming S355 steel mechanical properties can not meet state mechanical properties, and low-temperature impact energy is low. Impact ductility of Q345 series steel was improved by using heat treatment process of spheroidizing annealing and normalizing on the S355 steel. Through microstructure observation and data analysis, S355 has a fine uniform structure and its low-temperature impact energy can meet the requirements after spheroidizing annealing and normalizing. The steel plate of normalizing air-cooled steel plate has the highest low temperature impact energy and the best overall performance.

Keywords:S355; spheroidizing annealing ; Normalizing; Low temperature impact toughness

目   次

1  绪论 1

1.1  改善冲击功性能的方法 2

1.2  课题研究的来源和目的 6

2  实验材料、设备及方法 6

2.1  实验材料 6

2.2  热处理设备 6

2.3  球化退火的工艺方案 7

2.4  正火的工艺方案 9

2.5  课题研究过程 10

2.6  分析实验方法 10

3  课题研究结果与分析 12

3.1  对拉伸实验的分析 12

3.2  夏比冲击实验 18

3.3  金相组织的分析 19

结论 23

致谢 24

参考文献 25

1  绪论

    S355采用欧洲标准EN10025-2，由ECISS/TC10“结构钢等级及质量”技术委员会编制，相当于国标Q345D钢，要求-20℃冲击功达到34J以上。Q345D钢是一种含有少量合金元素的低合金高强度钢, 由于具有耐腐蚀、耐低温性能, 并且具有良好的加工工艺性能、焊接工艺性能和其它特殊性能被广泛应用于化工、石油、船舶、锅炉、压力容器等领域。用它来代替普碳钢，大大减轻结构重量，保证使用可靠、耐久[1]。论文网

Q345系列钢种包括Q345A、Q345B、Q345C、Q345D 和Q345E，属低合金高强度结构钢，由于该系列钢种具有良好的综合力学性能与工艺性能而在工程上被广泛应用[2]。该系列钢种不用热处理,直接使用, 成本较低, 是一种节约能源和资源的环保型钢种,但是由于不经过热处理直接满足条件要求，从而使该系列钢在力学性能上有一定的难点，尤其是对低温冲击韧度的要求，具体指标要求见表1.1。