摘要:本文以六亚甲基四胺和硝酸锌为原料,采用水热合成法在锌片上制备了氧化锌纳米阵列;用超声辅助化学沉积法制备CdS/ZnO纳米阵列,通过进一步反应掺杂纳米银制备CdS/ZnO/Ag纳米阵列,用扫描电镜(SEM)技术对其结构进行表征和分析。以甲基橙为目标物,比较了三种纳米材料的光催化性能。结果表明,纳米 CdS/ZnO与纳米ZnO相比,光催化性能有较大的提高,CdS/ZnO纳米阵列光催化剂经400W高压汞灯辐射 1。5小时,甲基橙溶液的降解率达到到78。8%;是氧化锌纳米阵列的1。25倍。CdS/ZnO/Ag纳米阵列的光催化性能略高于CdS/ZnO纳米阵列,CdS/ZnO/Ag纳米阵列在同样条件下,甲基橙溶液的降解率达到81。3%。本文还进一步探究了自然光下三种样品对酸性大红GR的光催化效果。实验表明,在同样的自然光下1。5个小时,ZnO ,CdS/ZnO,CdS/ZnO/Ag对酸性大红GR的降解率分别为64。6%,81。4%,86。9%,显然氧化锌复合材料的光催化性能与单纯氧化锌相比有明显的提高。72793

Abstract:In this paper, six methylene tetramine and zinc nitrate as raw materials, using hydrothermal synthesis method on the zinc was prepared by zinc oxide nanometer array; With ultrasonic assisted chemical deposition of CdS/ZnO prepared by nanometer array, by further reaction with preparation of silver nanoparticles CdS/ZnO/Ag nanoparticle arrays, by scanning electron microscopy (SEM) technology for characterization and analysis of its structure。 With methyl orange as the target, compares the three kinds of light catalytic properties of nanomaterials。With methyl orange as the target, the use of ultraviolet spectrophotometer compares three kinds of light catalytic properties of nanomaterials。 The results show that the CdS/ZnO/Ag photocatalytic performance of the array is slightly higher than the CdS/ZnO nanoparticle arrays, CdS/ZnO nanoparticle array light catalyst by 400 w high pressure mercury lamp radiation 1。5 hours, the degradation of methyl orange solution rate reached to 78。8%; Is 1。25 times that of the zno nanoparticle arrays。 CdS/ZnO/Ag photocatalytic performance of the array is slightly higher than the CdS/ZnO nanoparticle arrays, CdS/ZnO/Ag nanoparticle array under the same conditions, the degradation of methyl orange solution rate of 81。3%。 This article also explores the natural light of three samples of acid scarlet GR photocatalytic effect。 Experiments show that under the same natural light 1。5 hours, ZnO, and CdS/ZnO, and CdS/ZnO/Ag of acid scarlet GR degradation rate were 64。6%, 81。4%, 86。9%, obviously light catalytic properties of zinc oxide composites compared with pure zinc oxide has obvious enhancement。

毕业论文关键词:水热法;化学沉积法;ZnO纳米阵列膜;复合纳米阵列膜;光催化

Keyword: hydrothermal method; Chemical deposition; ZnO nanoparticle array ; Composite nanometer array membrane; photocatalysis

目录

1。 引言 3

1。1 研究背景 3

1。2研究意义 3

1。3 研究内容及要解决的问题 3

1。3。1  ZnO纳米阵列制备 3

1。3。2 CdS/ZnO纳米阵列制备 3

1。3。3。 CdS/Ag/ZnO纳米阵列制备 3

1。3。4 表征分析 3

1。3。5光催化实验 4

1。4 研究方法 4

1。4。1文献查阅法 4

1。4。2 实验法 4

1。5 国内外研究现状

上一篇:PVDF/ACM复合体系力学行为研究
下一篇:静电喷雾法制备TiO2多孔微球

过渡金属/锰复合氧化物热敏降解有机染料

聚丙烯及其复合材料的抗静电研究

基于碳纳米管的聚甲醛成核剂的设计与合成

含有银纳米粒子的POM/PLL...

BCC-Fe中螺位错与Cu纳米团簇...

锡酸锌纳米材料制备及其结构表征

纳米复合薄膜的制备与表征

我国风险投资的发展现状问题及对策分析

网络语言“XX体”研究

互联网教育”变革路径研究进展【7972字】

麦秸秆还田和沼液灌溉对...

张洁小说《无字》中的女性意识

LiMn1-xFexPO4正极材料合成及充放电性能研究

老年2型糖尿病患者运动疗...

安康汉江网讯

新課改下小學语文洧效阅...

ASP.net+sqlserver企业设备管理系统设计与开发