摘要：本文主要用购自北京的JAM-II膜作为主要的阴离子交换膜进行，并同时用所购买的上海阴离子交换膜和山东阴离子交换膜进行对比实验。通过实验最终确定使用JAM-II膜。同时使用扫描电镜（SEM）对阴离子交换膜进行必要的表征。结果表明所用于试验的阴离子交换膜由于种类、制作工艺的不同，其在扫描电镜下所呈现的表征图也不同。
- 上一篇：B、Mg、Al对DBAP燃烧剂燃烧性能影响研究
- 下一篇：MOF/石墨烯复合材料的组装及在超级电容器中的应用
本次课题中，主要用所购买的离子液体（1-辛基-3-甲基咪唑双三氟甲磺酰亚胺盐）作为主要的油相支持电解质，0.5M的氯化钾溶液作为水相支持电解质，构筑阴离子交换膜支撑的两互不相溶界面。
利用循环伏安法（CV）来研究在该界面上尺寸选择性离子转移反应。结果表明，使用阴离子交换膜所构筑的两互不相溶液液界面可以到到一个较宽的电化学窗口。（-0.5v-1.0v）并利用ClO4-、SO42-、NO2-阴离子来研究在该界面上的尺寸选择性离子转移反应。结果表明，该阴离子在此电化学窗口下发生了离子转移反应，既从水相转移到油相之中。20564
毕业论文关键字 ：阴离子交换膜；离子液体；两互不相溶界面；循环伏安；离子转移
Studies on the Electric charge Transfer Behaviors across the two Immiscible Interface Supported by Anion-Exchange Membrane
Abstract: in this paper, JAM-II membrane from Beijing was used as a main anion-exchange membrane, meanwhile, anion-exchange membranes from Shanghai and Shandong were also applied in this experiment. Through the research，JAM-II membrane was proved to the best one. The scanning electron microscopy (SEM) was used to characterize those above membrane materials, and the results show that different anion-exchange membranes had their own characteristics in SEM because of their different kinds and production process.
In the work, the commercially available room temperature ionic liquids ( 1-octyl-3- methylimidazolium bis(trifluoromethylsulfonyl)imide ) were used as main supporting electrolyte of oil phase, while potassium chloride solution which the concentration is 0.5M was used as supporting electrolyte of water phase, and then both of the phases were used to build two immiscible interface supported by anion-exchange membrane.
Using cyclic voltammetry (CV) method to study on size-selective ion transfer behaviors at this interface. And results show when using that two immiscible interface supported by anion-exchange membrane, I can get a better electrochemical window. (-0.5v-1.0v) ClO4-、SO42- 、NO2-anions were used to research the size-selective ion transfer behaviors at this interface. It shows that ion transfer reaction had taken place at this electrochemical window, which means ions had transfer from water phase to oil phase.
Keywords: anion-exchange membrane ；room temperature ionic liquids ；two immiscible interface ；cyclic voltammetry ；ion transfer
目录
1 绪论 1
1.1 选题研究目的和意义 1
1.2 选题研究现状及发展趋势 2
1.2.1 离子交换膜 2
1.2.2 双电层及Ｄｏｎｎａｎ理论 3
1.2.3 离子液体 4
1.2.4 离子液体/水界面电化学 5
2 实验部分 6
2.1 仪器与试剂 6
2.1.1 试剂 6
2.1.2 仪器 7
2.1.3 试剂与药品配制 8
2.2 实验内容 8
2.2.1 实验原理 8
2.2.2 阴离子交换膜的表征 9
2.2.3 构筑阴离子交换膜支撑的两互不相溶界面 9
2.2.4 研究在该界面上的尺寸选择性离子转移反应 10
2.2.5 实验流程图、示意图和装置图。 11
-
PS-b-PHEMA及其双组分嵌段共...
-
PS-b-PNIPAM单组份及其双组份...
-
生物降解食品保鲜膜的制备与应用研究
-
聚天青C/还原石墨烯杂化膜...
-
聚天青B与聚苯胺复合膜的...
-
钴膜修饰碳纤维电极测定磷酸二氢盐的研究
-
氧化锌/二氧化钛复合薄膜...
现代简约美式风格在室内家装中的运用
NFC协议物理层的软件实现+文献综述
上市公司股权结构对经营绩效的影响研究
浅析中国古代宗法制度
中国传统元素在游戏角色...
g-C3N4光催化剂的制备和光催化性能研究
江苏省某高中学生体质现状的调查研究
巴金《激流三部曲》高觉新的悲剧命运
高警觉工作人群的元情绪...
C++最短路径算法研究和程序设计