摘要当下科学技术日新月异，单一材料很难满足人们的要求。导电聚合物因其 独特的物理化学性质广泛用于光电转换、电催化、电致变色装置、充放电电池、 光电转换、充放电电池等领域。而本文主要介绍了聚天青 C 与还原石墨烯杂化 膜的电化学制备及其电化学性能的研究，主要使用了电化学法进行制备。用循 环伏安法合成聚天青 C 膜，再在上面滴加氧化石墨烯还原得到最终的产物，还 原使用的是安培法。杂化膜合成好之后，对杂化膜的电化学性能、电致变色性 能、谱学及形貌也进行了研究表征。83304

毕业论文关键词：导电聚合物;  聚天青 C;  还原石墨烯;  杂化; 电致变色

Abstract Currently, as both science and technology are developing rapidly, a single material can not meet the requirements of the people。 Due to theirs unique physicochemical properties, conductive polymers have been used widely in electrocatalysis, electrochromic devices, photovoltaic, charge and discharge batteries and other fields。 The paper introduces the research ene hybrid Preparation and electrochemical properties of polyethylene film electrochemical reduction of graphite and Azure C, was prepared mainly using electrochemical methods。 Cyclic voltammetry Poly Azure C film, then dropped in the above reducing graphene oxide to obtain a final product, reducing the use of the iPad。 After a good film hybrid synthesis of hybrid membrane electrochemical properties, electrochromic properties, genealogy and morphology were also studied to characterize。

Keywords: Conductive polymers; Azure C; reduced graphene; hybrid; electrochromism

目 录

第一章 绪论 1

1。1 研究背景 1

1。2 导电聚合物的概念 1

1。2。1 导电聚合物的制备方法 1

1。2。2 导电聚合物的研究方法 2

1。2。3 导电聚合物的特点 3

1。2。4 导电聚合物的应用 4

1。3 石墨烯的概念 4

1。3。1 石墨烯的研究历史及背景 4

1。3。2 石墨烯的特性 4

1。3。3 石墨烯的制备 5

1。3。4 氧化石墨烯的合成 6

1。3。5 石墨烯的应用和发展方向 7

1。4 聚天青 C 的概念 8

1。5 聚天青 C 与还原氧化石墨烯的复合 8

1。6 电致变色 8

1。7 论文的主要内容及设计思路 10

第二章 实验部分 11

引言 11

2。1 实验药品及器材 11

2。2 实验仪器 11

2。3 氧化石墨烯（GO）的制备 12

2。4 还原石墨烯的制备 12

2。5 聚天青 C 的制备 13

2。6  聚天青 C/还原石墨烯杂化膜的制备