摘要： 近年来，随着工业科技的发展，光催化剂的作用越来越突出。然而，传统的光催化剂具有适用范围小、容易造成二次污染的特点，纳米光催化剂的晶体直径小于100nm、运用成本低,故新兴的纳米光催化剂产业得到了社会各界的关注。采用水热合成法，以硝酸锌和乌洛托品为前躯体制备氧化锌纳米阵列，后以其为基质片，醋酸镍为镍源，采用水热法制备得到氧化镍和氧化镍/氧化锌复合纳米阵列，经焙烧得到光催化性能较好的材料。通过扫描电镜（SEM）、场发射透镜（TEM）和以酸性大红GR的降解脱色反应分别对样品结构形态进行表征和对样品的光催化性能进行试验。结果得到：ZnO纳米阵列的光催化性能高于NiO纳米阵列，NiO/ZnO（1:10）复合纳米阵列的光催化性能高于纯NiO、ZnO纳米阵列，并且NiO/ZnO(1:1)、NiO/ZnO(1:5)、NiO/ZnO（1：10）复合纳米阵列的光解率由39。6%提高至75。3%。89537

    Abstract：In recent years，with the development of industrial technology,the effect of photocatalyst is more and more prominent。However,the traditional photocatalyst has small applicable scope and is easy to cause secondary pollution 。The crystal diameter of photonanometer catalyst is less than 100 nanometer and it has low use cost ,so the emerging of photonanometer catalyst industry get the attention of the society from all walks of life 。Using hydrothermal synthesis method ,zinc nitrate and methenamine as body before preparation of zinc oxide nano array,,as the nickel source of nickel acetate,using hydrothermal calcination to get nickel/zinc oxide composite nano array。By scanning electron microscope (SEM) 、the field emission lens (TEM) and the degradation of acid red GR decolorizing reaction respectively characterizing the structure of the sample morphology and the photocatalytic properties of the samples to test。The results show that ：zinc oxide nano array photocatalytic performance is higher than the nickel oxide nano array ,nickel oxide/zinc oxide (1:10) composite nano array photocatalytic performance is higher than the nickel oxide、zinc oxide nano array and nickel oxide/zinc oxide(1:1)、nickel oxide/zinc oxide(1:5)、nickel oxide/zinc oxide(1:10)composite nano array of photolysis rate from 39。6% to 75。3%。源Q于W优E尔A论S文R网wwW.yOueRw.com 原文+QQ75201,8766

毕业论文关键词：水热合成法；氧化镍；氧化镍/氧化锌复合纳米阵列；光催化

Keyword: hydrothermal synthesis method; nickel oxide; nickel oxide/zinc oxide composite nano array;photocatalysis

目录

1。 引言 4

1。1 研究背景 4

1。2研究意义 4

1。2。1 理论意义 4

1。2。2 实践意义 4

1。3 研究内容及要解决的问题 4

1。3。1 ZnO纳米阵列的制备 4

1。3。2 NiO纳米阵列的制备 4

1。3。3 NiO/ZnO纳米阵列的制备 4

1。3。4 表征分析 4

1。3。5 光催化实验 4

1。4 研究方法 5

1。4。1文献查阅法 5

1。4。2 实验法 5

1。5 国内外研究现状 5

1。5。1国内研究现状 5

1。5。2国外研究现状 5

1。6 本文的研究思路内容和创新点