摘要本文研究了铝灰法制备PAC的新工艺的稳定性。以课题组提出的铝灰预处理得到的中性铝灰浆为原料，采用酸溶法制备得到PAC产品。采用VIS-723型分光光度计、AA240FS-GTA120原子吸收分光光度计、AFS-830原子荧光光度计、VISTA-MPX电感耦合等离子体发射光谱仪对反应原料、中性铝灰浆、产品及废渣的组成进行测定。采用激光粒度测试系统、SEM扫描电镜对其粒径和外观形貌进行表征。采用文献制备PAC方法，以3个不同来源和批次的铝灰为原料进行新工艺的稳定性验证。结果表明，该制备得到PAC产品，重金属离子除了Pb离子外其余检测均符合产品国标要求。反应原料、中性铝灰浆、产品及废渣的粒径大致范围在6.29~9.99μm范围内。定性验证实验所制备得到的PAC产品铝含量（以Al2O3计）和盐基度均达到了国标要求，平均值分别为10.40%、10.27%和10.30%，以及50.07、44.98和30.20。以上工作为本课题组以铝灰为原料制备PAC新工艺的进一步确定打下基础。26341
- 上一篇：聚乙二醇功能化含氟离子液体的设计与合成
- 下一篇：常规阻垢剂低温环境下作用效果研究
关键词 铝灰法 PAC制备 工艺 稳定性 原料 产物 表征
毕业论文设计说明书外文摘要
Title The New Preparing Technology of Polyaluminium Chloride from Aluminum Ash
Abstract
This paper studies the stability of a new process for preparation of PAC using aluminum ash. The PAC was obtained by using acid method, which used the neutral aluminum mortar as raw materials prepared by our research group. The composition of the raw materials, the neutral aluminum mortar, products and waste residue were analyzed by VIS-723 spectrophotometer, AA240FS-GTA120 atomic absorption spectrophotometer, AFS-830 atomic fluorescence spectrometer, VISTA-MPX inductively coupled plasma emission spectroscopy. Their particle size and appearance were characterized by laser particle size measurement system and SEM. The stability of the new process for preparation of PAC was verified by using 3 kinds of aluminum ash with different sources. The results showed that the metal ions were detected in the product and they were under the limitation of the national standard, except Pb. The dimension of the samples were within the range of 6.29~9.99μm. They were verified by the experiments that the alumina average amount and basicity of the product PAC were 10.40%, 10.27% and 10.30%, 50.07, 44.98 and 30.20, respectively. Those indicated that the process had made a well fundamental for the setup of the new process for preparation of PAC using aluminum ash.
Keywords aluminum ash, PAC preparation, process, raw material, product, characterization
目 录
1 引言 1
1.1 PAC的工业合成方法 1
1.1.1 活性氢氧化铝法 1
1.1.2 三氧化二铝法 1
1.1.3 结晶氯化铝法 2
1.1.4 铝灰法 2
1.1.5 铝灰制备PAC 2
1.2 存在问题 3
1.3 课题提出研究内容及研究意义 3
1.3.1 课题的提出 3
1.3.2 研究内容及意义 3
2 实验原理 5
3 实验方案设计 5
4 实验部分 7
4.1 实验仪器和药品 7
4.2 实验步骤 7
-
水热法制备SnO2纳米颗粒和性能研究
-
ZnO/碳纳米复合纤维的制备...
-
铁酸铋纳米颗粒制备和气敏性
-
sol-gel制备Sr掺杂的LaFeO3纳米颗粒和气敏性能
-
栗壳吸附质生物质活性炭的制备与应用
-
PS-b-PHEMA及其双组分嵌段共...
-
PS-b-PNIPAM单组份及其双组份...
巴金《激流三部曲》高觉新的悲剧命运
中国传统元素在游戏角色...
上市公司股权结构对经营绩效的影响研究
现代简约美式风格在室内家装中的运用
NFC协议物理层的软件实现+文献综述
g-C3N4光催化剂的制备和光催化性能研究
高警觉工作人群的元情绪...
C++最短路径算法研究和程序设计
浅析中国古代宗法制度
江苏省某高中学生体质现状的调查研究