    摘要FOX-7是一种新型高能钝感含能材料，其优异的综合性能引起世界各国的广泛关注。激光起爆技术是具有高安全性和高可靠性的新型起爆技术。本文针对FOX-7的激光直接起爆与激光驱动飞片起爆技术开展了初步的探索性研究。33376
    分析了纯FOX-7、2%碳纳米管/FOX-7、5%碳纳米管/FOX-7以及10%碳纳米管/FOX-7的微观形貌，测试了纯FOX-7、2%碳纳米管/FOX-7、5%碳纳米管/FOX-7以及10%碳纳米管/FOX-7的激光吸收性能。随着FOX-7炸药中碳纳米管掺杂量的增加，碳纳米管在FOX-7炸药颗粒上的分布愈发均匀；未掺杂碳纳米管的FOX-7的激光吸收性能极差，几乎将照射到药剂表面的激光完全反射；在FOX-7中掺杂碳纳米管有效提高了其对激光的吸收率。然而，在目前的实验条件下，采用自由振荡激光与调Q激光均未能将FOX-7成功起爆。
    研究并分析了装药压药密度分别为2.399g/cm3、2.256 g/cm3、2.212 g/cm3以及2.002 g/cm3条件下FOX-7炸药的激光驱动飞片起爆情况。虽然激光成功地驱动了飞片，但是FOX-7并未被成功起爆。
    关键词：FOX-7，激光起爆，激光驱动飞片，碳纳米管
    毕业论文设计说明书外文摘要
    Title   Experimental study on the initiation of FOX-7 laster
    Abstract:
    FOX-7 is a new energy insensitive energetic material, and its excellent comprehensive performance has caused wide attention in the world.. Laser initiating technology is a new initiating technology with high security and high reliability.. In this paper, the preliminary exploratory research on the laser direct detonation and the laser driven flyer initiation technology of FOX-7 is carried out.
    The pure FOX-7, 2% carbon nanotubes /FOX-7, 5% carbon nanotubes /FOX-7 and 10% carbon nanotubes /FOX-7 micro morphology analysis tested pure FOX-7, 2% carbon nanotubes /FOX-7, 5% carbon nanotubes /FOX-7 and 10% carbon nanotubes /FOX-7 laser absorption performance of. With increase of FOX-7 explosives in carbon nanotubes doped, carbon nanotubes in explosive FOX-7 particle distribution increasingly uniform; not doped carbon nanotubes FOX-7 laser absorption performance is poor, almost perfectly reflecting surface chemical laser irradiation; FOX-7 doped carbon nanotubes can effectively improve the rate of the absorption of the laser. However, in the present experimental conditions, the FOX-7 laser and the Q laser can not be successfully initiated by the free oscillating laser and the laser.
    The density of the explosive charge was studied and analyzed, and the laser driven flyer detonation of the FOX-7 explosive was 2.399g/cm3, 2.256 g/cm3, 2.212 g/cm3 and 2.002 g/cm3 respectively.. Although the laser successfully drives the flyer, the FOX-7 has not been successfully initiated.
    Keywords: FOX-7, laser initiation, laser driven flyer, carbon nanotube
    目   次
    1 绪论    1
    1.1 激光起爆技术概述    1
    1.2 激光起爆炸药的机理    3
    1.3 本文研究内容    4
    2 FOX-7的形貌与性能分析    5
    2.1 FOX-7的表面形貌分析    5
    2.1.1 FOX-7的宏观形貌    5
    2.1.2 FOX-7的微观形貌    6
    2.2 F0X-7的爆炸性能分析    11
    2.3 FOX-7的光学性能分析    11
    2.4 小结    15
    3 激光起爆FOX-7的实验研究    17
    3.1 实验装置与方法    17
    3.1.1 实验仪器介绍    17
    3.1.2 激光的稳定性    18
    3.1.3 激光的光束特性    18
    3.1.4 激光起爆FOX-7炸药的实验方法    19
    3.2 实验结果与分析    21
    3.2.1 实验结果    21
    3.2.2 实验分析    22
    3.3 小结    22
  1. 上一篇：氮掺杂石墨烯改性电极在生物电化学体系中的应用研究
  2. 下一篇：二维硫化镍基复合材料的制备及其性能研究

  1. WnCu团簇的结构和性能研究

  2. ZnO/碳纳米复合纤维的制备...

  3. sol-gel制备Sr掺杂的LaFeO3纳米颗粒和气敏性能

  4. 碳化硅改性水性聚氨酯的研究

  5. 栗壳吸附质生物质活性炭的制备与应用

  6. WO3-PbO2/C混合电容器的组装及性能研究

  7. Cu配合物的合成与分离乙烯/乙烷的性能研究

  8. 现代简约美式风格在室内家装中的运用

  9. g-C3N4光催化剂的制备和光催化性能研究

  10. NFC协议物理层的软件实现+文献综述

  11. 巴金《激流三部曲》高觉新的悲剧命运

  12. 上市公司股权结构对经营绩效的影响研究

  13. C++最短路径算法研究和程序设计

  14. 高警觉工作人群的元情绪...

  15. 浅析中国古代宗法制度

  16. 中国传统元素在游戏角色...

  17. 江苏省某高中学生体质现状的调查研究

　　

About

优尔论文网手机版...

主页：http://www.youerw.com

关闭返回