摘要纳米二氧化钛因为它拥有无毒性、价格低和对光照的稳定等一系列优点，被认为是目前最具有潜力的光学催化材料之一，而且基于二氧化钛的光催化技术可以很好地解决当前的良好环境材料的开发和能源问题而具有重要的研究意义。但是二氧化钛作为光催化材料存在两个问题需要解决：一是解决二氧化钛的光催化半导体载流子高复合率而导致的光催化效率低的问题；二是解决二氧化钛催化剂对可见光利用率低而导致光催化效率低的问题。本文为了解决上述的问题，采用了具有核壳结构的Ag@TiO2纳米线，这样不仅可以使TiO2有较大长径比结构，而且金属核可以作为光生电子的临时存储地方，降低光生电子空穴的复合几率，以此来提高光催化效果。并且，通过改变掺杂的Ag含量或者钛酸四丁酯量的条件，得到不同尺寸比例的Ag@TiO2纳米线，用光降解亚甲基蓝实验来测试所制样品的光催化性能，研究了不同尺寸比例的Ag@TiO2纳米线催化性能，从而寻找光催化效率最高的Ag@TiO2比例。38535
- 上一篇：基于ENVI的徐州市气溶胶反演
- 下一篇：YbLu2O3透明陶瓷的制备及其光学性能研究
毕业论文关键词: Ag@TiO2纳米线可控制备 核壳结构 光催化降解
Study on preparation and photocatalytic properties of Ag-TiO2 nanowires
Abstract：
Titanium dioxide nanoparticles which has no toxicity, low price and stable to light and a series of advantages are one of the most promising optical catalytic materials.Titanium dioxide photocatalytic technology can solve the problem of energy development and good environment of the current material.But the pure TiO2 has two problems as a good photocatalytic material: one is the low quantum efficiency of photocatalytic semiconductor carrier high recombination rate of titanium dioxide and lead the problem; the other is that the TiO2 catalyst of thesunutilization rate is low due to low quantum yield problems.In order to solve these bottleneck, we fabricated the Ag@TiO2 nanowires with core-shell structure .This not only can make the TiO2 structure with large length diameter ratio, but also the metal core can be used as a temporary storage place of photogenerated electrons.So it can reduce the recombination rate of photogenerated electron hole to improve the photocatalytic effect. Moreover, the Ag@TiO2 nanowires with different size ratio were obtained by changing the doping content of Ag or four butyl titanate content conditions. The photocatalytic properties of the samples was tested by the methylene blue photodegradation experiments. Furthmore, the effect of the catalytic properties of Ag@TiO2 nanowires on different sizes was studied to find the highest photocatalytic efficiency ratio of Ag@TiO2 nanowires.
Key words: Ag@TiO2 nanowires controlled synthesis Core shell structure
Photocatalytic degradation
目录
摘要： 1
Abstract： 2
第一章绪论 4
1.1 引言 4
1.2纳米光催化材料的综述 4
1.2.1光催化材料的介绍 4
1.2.2纳米材料的基本特性 5
1.2.3纳米光催化材料 5
1.3 纳米二氧化钛光催化剂的简介 6
1.3.1 TiO2的结构特点 6
1.3.2 纳米TiO2的合成方法 7
1.4 TiO2光催化原理及等离激元效应 8
1.5 影响TiO2光催化效率的因素 9
1.5.1粒径对纳米TiO2光催化效率的影响 9
1.5.2晶相对TiO2光催化效率的影响 9
1.5.3影响TiO2光催化效率的其他因素 10
1.6 TiO2核壳结构纳米材料的综述 10
1.6.1核壳结构材料研究现状 10
-
水热法制备SnO2纳米颗粒和性能研究
-
ZnO/碳纳米复合纤维的制备...
-
铁酸铋纳米颗粒制备和气敏性
-
sol-gel制备Sr掺杂的LaFeO3纳米颗粒和气敏性能
-
Co3O4和Fe3O4/WO3纳米材料的合...
-
纳米钛酸钡掺杂稀土元素...
-
紫外纳米转印材料的合成
g-C3N4光催化剂的制备和光催化性能研究
巴金《激流三部曲》高觉新的悲剧命运
高警觉工作人群的元情绪...
上市公司股权结构对经营绩效的影响研究
浅析中国古代宗法制度
中国传统元素在游戏角色...
现代简约美式风格在室内家装中的运用
C++最短路径算法研究和程序设计
NFC协议物理层的软件实现+文献综述
江苏省某高中学生体质现状的调查研究