摘要采用液-液界面法，获得了尺寸不同、形貌各异的硫化镉纳米晶。研究了水浴条件下，反应物浓度、反应温度以及反应时间对所合成硫化镉纳米晶微观结构、形貌等的影响，采用TEM、SEM、XRD、UV-DRS、PL等方法对产物的形貌、结构及性能进行表征。研究表明不同反应条件对产物形貌有一定的影响, 控制反应条件可以获得不同形貌的硫化镉纳米晶。并探讨了硫化镉纳米晶体的生长机理。另外，采用水热法制备了CdS纳米晶，探讨了反应条件对CdS纳米晶形貌的影响。63921

毕业论文关键词：纳米硫化物  液-液界面法  水热合成法

Title Liquid-liquid interfacial synthesis of single-crystalline CdS nanoparticle and Structural characterization

Abstract By using liquid-liquid interfacial method, the cadmium sulfide (CdS) nano-crystalline with different size and morphology was synthesized. The reactions were carried out in water bath. The effect of reactant concentration, reaction temperature and reaction time to the morphology and microstructures of CdS nano-crystalline was studied. TEM, SEM, XRD, UV-DRS, PL were used to characterize the synthesized CdS nano-crystalline. The results shows that the reaction conditions have impact on the morphology of the resultants. CdS nano-crystalline with different morphology can be achieved by changing the reaction conditions. The growth mechanism of CdS nano-crystalline was discussed. CdS nano-crystalline was also synthesized by adopting hydrothermal method. The effects of reaction conditions to the CdS nano-crystalline morphology were also discussed.

Keywords  Nano-sulfide liquid-liquid interface method hydrothermal method 

1  绪论 1

1.1 纳米材料 1

1.1.1 纳米材料的特性 1

1.1.2 纳米材料制备方法 2

1.2 硫化镉纳米材料 2

1.2.1 硫化镉纳米晶的制备方法 3

1.2.1.1 固相法 3

1.2.1.2 液相法 3

1.2.1.3 气相法 5

1.2.1.4 其他方法 6

1.2.2 硫化镉纳米晶的研究现状 6

1.2.3 硫化镉纳米晶的应用 6

1.3 本课题的主要内容 8

2  液-液界面法制备CdS纳米晶及表征 8

2.1 实验部分 9

2.1.1 实验试剂和仪器 9

2.1.2 液-液界面法制备CdS的原理 9

2.1.3 CdS的制备 10

2.1.4 表征手段 11

2.2 CdS结构及性质表征 12

2.2.1 XRD分析 12

2.2.2 形貌表征 13

2.2.3 Raman光谱分析 16

2.2.4 荧光光谱分析（PL） 17

2.2.5 固体紫外-可见光谱（UV-DRS）分析 17

3  水热法制备CdS纳米晶 18

3.1 实验部分 18

3.1.1 实验试剂和仪器 18

3.1.2 CdS的制备 19

3.2 CdS结构及性质表征