摘要随着办公自动化与信息化的发展,对快速输出高清晰的彩色图像和文字提出了更高的要求,传统熔融粉碎法制备的墨粉粒径较大,粒形不规则,导致打印质量下降。因此,通过化学聚合法制备彩色墨粉已成为研究的主要方向。本文利用细乳液聚合制备彩色墨粉用乳胶粒子,并通过凝聚技术和微胶囊技术,最终制备符合打印机实际需要的粒径及粒径分布的彩色墨粉。

通过纳米乳胶粒子凝聚复合制备微米复合粒子的实验研究,研究纳米乳胶粒子凝聚复合、粒径控制及固结成型的原理及工艺方法,掌握乳液聚合法彩色墨粉复合粒子的制备方法,实现各功能组分粒子的复合包覆及粒径的稳定控制;了解彩色墨粉复合粒子粒径、形貌、性能表征方法。实验发现:当絮凝剂用氯化铝,体系浓度20mmol/L,搅拌速度为200r/min,熟化时间30min,温度为95度时凝聚效果比较好。64133

毕业论文关键词 彩色墨粉 复合粒子 乳胶粒子 凝聚 微胶囊

 毕业设计说明书(论文)外文摘要

Title   The cohesion of color toner used nano latex particles  prepared by mini-emulsion polymerization

Abstract With the development of office automation and information technology, fast output high-definition color images and text put forward higher requirements, traditional melt crushed prepared toner particle size, grain shape is irregular, resulting in deterioration in print quality. By chemical polymerization method color toner has become the main direction of the study In this paper, the fine emulsion polymerization color toner latex particle, and by cohesion technology and microencapsulation technology, the final preparation of the actual needs of the particle size of the composite printer, the color toner particle size distribution.

Experimental study through the latex nanoparticles cohesion composite prepared micron composite particles, the nano-latex particles to agglomerate composite, particle size control and consolidation molding principle and process of the master color toner of the composite particles of the emulsion polymerization method, preparation method thereof, realizing the functions component composite coated particles and particle size stability control; understand the composite color toner particle size, morphology, Characterization method.

It was found that: When using aluminum chloride as flocculants, system concentration 20mmol / L, stirring speed 200r/min, aging time 30min, aging temperature 95 degrees ,the cohesion results were better.

Keywords  color toner, Composite particles,Latex particles,Cohesion,Microcapsules

目录

1  绪论 1

1.1  彩色墨粉的概述 1

1.2  彩色墨粉性能 3

1.3  细乳液法制备彩色墨粉 4

1.3.1  细乳液聚合法制备彩色乳胶粒子机理分析 4

1.3.2 乳胶粒子的凝聚复合的机理分析 5

1.4本课题研究目的以及研究内容 7

2  彩色墨粉纳米乳胶粒子的制备 8

2.1 实验试剂与仪器 8

2.2 实验过程 10

2.2.1 实验单体与引发剂的提纯 10

2.2.2 细乳液制备及聚合过程 10

2.2.3实验表征 11

2.3 实验结果 11

3 彩色墨粉纳米乳胶粒子的凝聚复合

上一篇:溴化丁基橡胶耐热性能研究
下一篇:挠性覆铜板用热塑性聚酰亚胺胶膜的制备及性能

多巴胺的自聚及其对碳纳米管的改性

聚集诱导发光性质研究进展

超分子聚合物凝胶的制备

金属配位作用的热响应性...

壳聚糖介导的液固提取黄连中的生物碱

石墨烯聚合物的复合体系的制备和性质

Fe3MoS6/N-S共掺杂TiO2/聚苯胺复合物的制备表征

网络语言“XX体”研究

LiMn1-xFexPO4正极材料合成及充放电性能研究

麦秸秆还田和沼液灌溉对...

老年2型糖尿病患者运动疗...

安康汉江网讯

互联网教育”变革路径研究进展【7972字】

ASP.net+sqlserver企业设备管理系统设计与开发

我国风险投资的发展现状问题及对策分析

新課改下小學语文洧效阅...

张洁小说《无字》中的女性意识