摘要本文主要研究了系列化 PDMC 结构与性能的关系。本实验采用 APS 作为引发 剂，合成了不同特征黏度值的 PDMC 系列化产物，并对特征黏度值为 2﹑4﹑6﹑8

﹑10dL·g-1 的 PDMC 系列产物进行精制。将精制后系列化产物进行红外核磁和热 分析，得到产物结构、性质和性能的关系。通过改变 DMC 和 APS 起始含量，能 够控制 PDMC 产物的特征黏度值。研究发现 PDMC 的第二分解阶段属于一级反应， 且热分解焓变和热分解活化能随着相对分子质量增加而增加，这就证明 PDMC 特 征黏度值越高，热稳定性就越好。68556

毕业论文关键词 PDMC 系列化表征 热分析 结构与性能

Title The relationship between structure and properties of PDMC series products

Abstract

The relationship between structure and properties of the series PDMC was studied in this paper. Using APS as an initiator, PDMC products with series different intrinsic viscosity were synthesized and purified. The PDMC series products with intrinsic viscosity 2, 4, 6, 8, 10dL • g-1 were characterized by FTIR, NMR and thermal analysis.The results showed: PDMC intrinsic viscosity could be controlled by the start mass fraction of DMC and APS. Second decomposition stage of PDMC was first-order reaction, and the thermal decomposition enthalpy and activation energy increase with relative molecular mass increaseing, which prove the higher PDMC intrinsic viscosity , the better the thermal stability was.

目 次

1 引言 1

1.1 DMC 单体及其均聚物简介 1

1.2 PDMC 生产现状 1

1.3 系列化 PDMC 结构与性能的研究现状 2

1.4 PDMC 合成研究现状 3

1.5 研究内容及意义 4

2 实验部分 6

2.1 实验试剂 6

2.2 实验仪器 6

2.3 实验原理 7

2.4 实验设计 10

2.5 实验步骤 11

2.6 实验结果与讨论 12

2.7 问题讨论 21

3 结论 23

致谢 24

参考文献 25

附录 26

1 引言

目前比较常用的阳离子单体有甲基丙烯酰氧乙基三甲基氯化铵(DMC)、二甲基二 烯丙基氯化铵（DMDAAC）、丙烯酰氧乙基三甲基氯化铵（DAC），以其为基制备的 均聚物和共聚物在诸多领域有着重要用途。其均聚物和与丙烯酰胺（AM）共聚形成 的共聚物（统称为阳离子聚丙烯酰胺，简称CPAM）由于具有分子量可控、阳离子度 可调、稳定性高、水溶性好等优点，广泛应用于石油开采、造纸、采煤、纺织印染、 医药、生物、日用化学品、水处理等领域[1,2]。由于聚合物的用途决定于单元结构和相 对分子质量，不同相对分子质量的PDMC具有不同的应用性能。所以，系列化相对分 子质量PDMC结构与性能的研究具有重要意义。