摘要：本文通过对抗菌剂PHMG合成，通过直接反应法、缩合剂DIC法和缩合剂EDCI法三种改性方法制得了丙烯酸改性抗菌剂PHMG；并通过红外分析、氮元素测试和核磁分析对丙烯酸改性抗菌剂进行了结构表征及性能测定。并确定丙烯酸接枝抗菌剂的最佳制备条件。研究表明，三种方法都能将丙烯酸接枝到抗菌剂上。20465
关键字：抗菌剂；丙烯酸改性抗菌剂；抗菌性；性能；缩合剂
The preparation and modification of antibacterial PHMG
Abstract: In this paper, the synthesis of antimicrobial PHMG direct reaction modified DIC condensing agent and a condensing agent EDCI Modification Act Three methods have been modified acrylic modified antimicrobial PHMG; characterized by IR, NMR analysis of nitrogen testing and three methods to test out the performance of modified acrylic modified antimicrobial agent after different methods. And understand how to use the different conditions of the modified method for preparing a modified acrylic modified antimicrobial acrylic graft maximum rate, so that the best kind of modification conditions. Research shows that the three methods can be modified acrylate grafted onto an antibacterial agent.
Keywords: Antimicrobial agents; acrylic-modified antimicrobial agent; antimicrobial; performance; condensing agent
目 录
1．绪论 4
1.1抗菌剂PHMG的概述 4
1.1.1抗菌剂PHMG简介 4
1.1.2抗菌剂PHMG的制备 4
1.2胍类衍生物的概述 5
1.2.1胍类衍生物的应用 5
1.2.2几种聚优尔亚甲基胍的衍生物 6
1.3抗菌剂PHMG改性的概述 7
1.3.1抗菌剂PHMG的改性研究现状 7
1.4本课题的研究目的与意义 9
2试验 9
2.1原料名称、规格和来源 9
2.2抗菌剂PHMG的合成机理和改性机理 10
2.2.1抗菌剂PHMG的合成机理 10
2.2.2丙烯酸改性PHMG的机理 10
2.3抗菌剂PHMG的合成及其改性制备工艺 12
2.3.1抗菌剂PHMG的合成制备工艺 12
2.3.2直接反应法改性抗菌剂PHMG的制备工艺 12
2.3.3DIC缩合法改性抗菌剂PHMG的制备工艺 13
2.3.4 EDCI缩合法改性抗菌剂PHMG的制备工艺 13
2.4性能测试 14
2.4.1红外光谱测试 14
2.4.2氮元素分析 14
2.4.3核磁共振测试 15
3.结果与讨论 15
3.1抗菌剂PHMG改性方法的选择 15
3.2改性抗菌剂改性工艺的条件控制 16
3.3不同方法接枝双键对于抗菌剂PHMG结构的影响 16
3.3.1温度对直接反应法改性抗菌剂PHMG结构的影响 16
3.3.2DIC缩合剂的量对DIC缩合法改性抗菌剂PHMG结构的影响 17
3.3.3EDCI缩合剂的量对EDCI缩合法改性抗菌剂PHMG结构的影响 18
3.4不同方法接枝双键对于氮元素含量的影响 19
3.4.1 温度对直接反应法改性抗菌剂氮元素含量的影响 19
3.4.2 DIC缩合剂含量对DIC缩合法改性抗菌剂氮元素含量的影响 20
3.4.3 EDCI缩合剂含量对EDCI缩合法改性抗菌剂氮元素含量的影响 21
3.5不同方法接枝双键对于抗菌剂核磁测试的影响 23
3.5.1 抗菌剂PHMG的核磁测试 23
3.5.2 直接反应法改性抗菌剂的核磁测试 24
3.5.3 DIC缩合法改性抗菌剂的核磁测试 25 抗菌剂PHMG制备及改性研究:http://www.youerw.com/yixue/lunwen_12246.html