摘要以具有刚性链结构的对苯二胺（PPD）和联苯四甲酸二酐（s-BPDA）聚代PMDA/ODA体系PI中的二酐和二酐，制备PI薄膜，并以Talc进行复合改性。考察了单体含量种类及Talc对PI薄膜力学性能及动态热机械性能的影响。结果表明PPD及s-BPDA均有有效提高PI薄膜的力学性能，其中又以PPD对薄膜弹性一模量的影响最为显著。Talc的引入也能进一步提高PI薄膜的刚性。并且经KH171处理后，PI薄膜的拉伸强度也有大幅提高。88240

Abstract It is common to produce the PI film with replacing the monomer of the PMDA/ODA with the PPD and s-BPDA which possess structure of rigid chain and compound modified with the Talc, which inspect the content and species of monosome and the influence that the Talc act on the PI film mechanical property and dynamic mechanical property。 Study results signify PPD and s-BPDA can enhance the mechanical property of PI film。 In especial, PPD have an effect on elasticity of the thin film。 Talc can improve the rigid of PI film。 The tensile strength of PI film has been enhanced prominently after KH171 deal。 

毕业论文关键词：高弹性模量；聚酰亚胺薄膜；滑石粉

Keyword: High elastic modulus； Polyimide films； talcum powder

目    录

1引言 1

1。1研究源-于,优W尔Y论L文.网wwW.youeRw.com 原文+QQ75201,8766背景 1

1。2研究的基本内容 3

1。2。1 研究的基本内容 3

1。2。2 拟解决的主要问题 3

1。3拟采取的研究方法及措施 3

2实验 4

2。1主要的原料与试剂 4

2。2 实验仪器 4

2、H电热恒温鼓风干燥器，生产厂家为上海精宏实验设备有限公司。 5

2。3 试样制备 5

2。3。1  PI薄膜的制备 5

2。3。2 滑石粉填充PI薄膜的制备 6

2。4 测试与表征 6

1、力学性能测试与表征 6

3结果与讨论 7

3。1 反应单体组成对PI薄膜性能的影响 7

3。1。1 s-BPDA对(s-BPDA/PMDA)/ODA体系PI薄膜力学性能的影响 7

3。1。2 PPD对PMDA/(PPD/ODA)体系PI薄膜力学性能的影响 8

3。1。3 (s-BPDA/PMDA=6:4)/(ODA/PPD)体系PI的DMA分析 10

3。2 滑石分（Talc）（表面处理、含量、粒径）对PI薄膜性能的影响 10

3。2。1 Talc对PI薄膜弹性模量的影响 11

3。2。1 Talc对PI薄膜拉伸强度的影响 12

3。2。3 Talc含量对PI薄膜性能的影响 13

3。2。4 Talc含量对PI薄膜储能模量的影响 13

3。3 Talc对PI薄膜透光学性能的影响 14

3。3。1 Talc含量对PI薄膜透光率以及From~优E尔L论E文W网wWw.YoUeRw.com 加QQ7520.18766雾度的影响 14

4结论 16

参考文献 高模量聚酰亚胺薄膜的制备与表征:http://www.youerw.com/cailiao/lunwen_156919.html