摘 要：利用异氰酸乙酯对凹凸棒土进行改性并利用红外、X射线衍射、比表面等对改性前后凹凸棒土进行表征。结果表明，异氰酸乙酯有效地以化学键的形式结合到凹凸棒土表面，但没有改变凹凸棒土层状构造。测定了改性后的凹凸棒土对吡蚜酮的吸附能力。在吡蚜酮浓度为50 mg/L 溶液中加入0。35 g 改性凹土，在26。8 ℃，pH=8的条件下反应1。5 h，对吡蚜酮吸附率为最佳，达到91%以上。93170
毕业论文关键词：异氰酸乙酯，凹凸棒土，有机改性，吡蚜酮，吸附
Abstract：Attapulgite powders were organically modified using ethyl isocyanate。 The pristine and modified attapulgite powders were characterized by IR, XRD, BET。 The results showed that the main interaction between attapulgite surface and ethyl isocyanate are chemical bonds。 The adsorption performance of pymetrozine on the modified attapulgite was investigated under different time, pH, dosage of adsorbent and temperature conditions。 The results showed that the adsorption of pymetrozine on the modified attapulgite was strongly dependent on pH and adsorption time。 The adsorption capacity was 91 % at room temperature, 0。35 g dosage, pH=8 and 1。5 h adsorption time。 This revealed that the attapulgite powders can be a prospective sorbent for pre-concentration of pymetrozine from solutions in environment。
Keyword: ethyl isocyanate, attapulgite powder, modify, pymetrozine, adsorption
目 录
1 前言 4
2 实验部分 4
2。1 试剂和仪器 4
2。1。1 试剂 4
2。1。2 仪器 4
2。2 改性凹凸棒土的制备 4
2。2。1 凹凸棒土的盐酸处理 4
2。2。2 氨基凹土的制备 4
2。2。3 改性凹凸棒土的制备 5
2。3 改性凹土对吡蚜酮来自优O尔P论R文T网WWw.YoueRw.com 加QQ7520`18766 的吸附实验 5
3。 结果与讨论 5
3。1 改性凹凸棒土的表征 5
3。1。1 红外光谱分析 5
3。1。2 X-射线(XRD)分析 7
3。1。3 比表面分析 9
3。2 改性凹凸棒土对吡蚜酮吸附测试 10
3。2。1 吡蚜酮标准曲线的确定 10
3。2。2 改性凹土的加入量对吸附平衡的影响 11
3。2。3 时间对吸附平衡的影响 12
3。2。4 温度对吸附平衡的影响 13
3。2。5 pH对吸附平衡的影响 15
结论 16
参考文献 17
致谢 18
1 前言 论文网
凹凸棒土是一种具有独特的层链状结构特征的晶质水合镁铝硅酸盐矿物，在江苏省眙盱县境内分布广泛，占全国凹土储藏量的73%，有着“千土之土”的美誉。然而我国凹土利用率低，附加产品开发应用少，价格低廉[1]。作为农业大国，我国农药除草剂的使用量大，对环境造成了破坏。因此选择一种吸附试剂用以去除水体中残留农药具有非常重要的前景[2-3]。本文考虑以异氰酸乙酯对凹凸棒土进行有机改性[4-6]，测试改性后的凹凸棒土对杀虫剂吡蚜酮的吸附能力，为以后利用凹凸棒土处理农业污染提供依据。 异氰酸乙酯改性凹凸棒土的制备以及对吡蚜酮吸附研究:http://www.youerw.com/huaxue/lunwen_200973.html