摘 要：以凹凸棒土作为水质净化微生物制剂中的吸附载体，并分别以热处理、酸处理、盐处理对其进行改性后，混合耐高盐的水质净化菌株，制成凹凸棒土-复合微生物制剂。 以生活污水为处理对象进行室内实验，结果显示，以 220℃下处理 2 小时的热改性后凹凸 棒土-复合菌剂的 CODcr 去除率最大，高达 71。7％；1mol/L 的硫酸改性处理后 pH 的下降最 大，pH 为 6。27，下降了 41。94％；2mol/L 的 NaCl 改性后脱色效果最佳，脱色率为 57。09％。75621

毕业论文关键词：微生物制剂，凹凸棒土，水质净化

Abstract：Attapulgite was used as adsorption carrier of microbial agents for purifying water

and treated by calcine, acid, inorganic salt。 Then we mixed the midified attapulgite with strains which owns high resistant to salt, made it into complex attapulgite-microbial agents。 After experiment of domestic sewage, the result showed that the highest removal rate of 71。7% could

be achieved for CODcr based on temperature at 220℃ for 2 hours attapulgite; the pH was 6。27

and the 41。94% fall on pH was the largest with 1mol/L sulfuric acid modified attapulgite; the decolorization effect of 2mol/L NaCl modified attapulgite was best and the decolorization rate was 57。09%。 The paper provided valuable experimental data for modifying attapulgite and applying to treating domestic sewage。

Keywords：microbial   preparation，attapulgite，water   purification

目 录

一、研究背景 4

1 前言 4

2 凹凸棒土简介 4

3 凹凸棒土常见改性方法 5

3。1 热改性 5

3。2 酸改性 5

3。3 超声波改性 6

3。4 有机改性 6

二、研究改性凹凸棒土-微生物制剂对污水净化作用的试验 7

1 材料与方法 7

1。1 试验材料 7

1。2 试验方法 8

1。2。1 目的菌株的分离纯化与培养 8

1。2。2 凹凸棒土的制备 9

1。2。3 凹凸棒土的改性处理 9

1。2。4 改性凹土-微生物菌剂的制备 9

1。2。5 污水的采集 9

1。3 改性凹土-微生物菌剂的污水处理效果 9

2 结果分析 11

结论 13

参考文献 14

致谢 15

一、研究背景

1    前言

目前，污水废水的处理方法主要有物理法、化学法、生物处理法三大种。其中，生物 处理法是指利用微生物的生理代谢活动，吸附或降解水中的有毒有害物质，从而稳定、无 害地降解水中各种有机与无机污染物。而在生物处理法中，水质净化微生物制剂是较为常 用的方法之一，制剂主要由目的菌株（多为芽孢杆菌属（Bacillus）及少数真菌）、吸附载 体（多为活性炭、凹凸棒土等多孔材料）、保护剂（多为羧甲基纤维素钠）组成，常为粉 剂或水剂。水质净化微生物制剂中的吸附载体会影响污水的净化效果，不同吸附材料具有 不同的吸附性、胶体性、无毒性、絮凝性等，这些理化性质直接影响净水微生物的活性以 及作用发挥。论文网 (责任编辑：qin)