摘要MgZnO 半导体薄膜作为一种原料来源广泛，价格低廉，无毒无害的新型光电材料，通过实现禁带宽度的连续可调，使其作为一种宽带隙材料受到了大家的关注。人们通过改变 Mg 的含量、溅射功率等一系列因素来实现 MgZnO薄膜的禁带宽度在一定范围内连续可调，从而制备得到广泛适用于蓝光至紫外光谱区域的发光器件，使得其运用越来越广泛。本实验采用了射频磁控溅射法通过改变溅射功率和氩氧比成功的在硅片和玻璃衬底上沉积了非晶MgZnO薄膜，并通过XRD、SEM、PL和透过率的检测手段对薄膜的结构和光学特性进行了分析。非晶 MgZnO薄膜表面平整光滑，结晶性差，在不同溅射功率作用下的峰位变化很小，为近紫外发光，氩氧比的改变使得Mg没有与衬底很好的结合，薄膜在可见光范围内具有很高的透过率，溅射功率的变化使得其带隙逐渐往紫外区变化。 21599
- 上一篇：激光熔覆技术制备网状衬垫的工艺研究
- 下一篇：圆形焊接螺母与镀锌钢板的凸焊工艺试验研究
关键词 非晶MgZnO 薄膜 结构性能 光学性能
Title Preparation and Photodetector research of MgZnO films
Abstract
MgZnO semiconductor films have absorbed much attention as a kind of new
photovoltaic materials for wide band gap, broad sources of raw
materials, low price and nontoxic by implementing adjustable band gap
continuously. The band gap of MgZnO films has been achieved adjustable
continuously within a certain range by varying the content of Mg,the
sputtering power and other factors. As a result,the light-emitting
device has been prepared which was widely used in Blu-ray to ultraviolet
spectrum region to make its use more widely. By controlling sputtering
power and argon oxygen ratio, RF magnetron sputtering has been used to
deposit amorphous MgZnO thin film on silicon and glass substrates. The
structure and optical properties of the films were analyzed through
detection means of XRD, SEM, PL and transmittance. Experimental results
show that amorphous MgZnO films have smooth surface and poor
crystallinity. There is little change in position of the peak at
different sputtering power and it is near ultraviolet light-emitting.
The change in the ratio of argon-oxygen can not make Mg have a good
combination with the substrate. The film has a high transmittance in
the visible range and the change of the sputtering power makes its band
gap gradually change to the ultraviolet region.
Keywords amorphous MgZnO films structural characteristics optical properties
目录
1 引言 . 1
1.1 MgZnO薄膜的制备方法 1
1.2 磁控溅射中 MgZnO薄膜性能的影响因素. 3
1.3 MgZnO光电探测器存在的主要问题和发展趋势.. 4
1.4 MgZnO薄膜的研究进展 4
1.5 本课题的研究内容 5
2 MgZnO薄膜的制备及流程 6
2.1 磁控溅射设备 .. 6
2.2 试验参数 . 7
2.3 样品制备流程及注意事项 7
2.4 样品的分析与表征方法 . 8
3 结果分析与讨论 10
3.1 MgZnO薄膜结构特性研究 10
3.2 MgZnO薄膜的光学特性分析.. 19
结 论 . 23
致 谢 . 24
参考文献 25
-
电弧离子镀TiAlN硬质薄膜的制备及性能研究
-
电弧离子镀TiCN硬质薄膜的制备及性能研究
-
ZK60表面MAO-ED陶瓷/HA复合生物涂层的制备
-
水性环氧树脂的制备及性能研究
-
固含量对流延成型法制备...
-
干压成型法制备xBaTiO3/(1...
-
铅离子印迹多孔材料制备及性能研究
中国传统元素在游戏角色...
NFC协议物理层的软件实现+文献综述
上市公司股权结构对经营绩效的影响研究
g-C3N4光催化剂的制备和光催化性能研究
巴金《激流三部曲》高觉新的悲剧命运
C++最短路径算法研究和程序设计
高警觉工作人群的元情绪...
浅析中国古代宗法制度
江苏省某高中学生体质现状的调查研究
现代简约美式风格在室内家装中的运用