摘要： 本文对Al-Ti-B2O3系和Ti-B4C系，运用原位反应法分别成功制备出了钛基复合材料（Al2O3+TiC）/Ti和（TiB2 +TiC）/Ti，并运用SEM、EDS、XRD及DSC等现代手段对反应过程及反应结果进行了全面分析。研究结果表明：随着增强体体积分数增加，反应激烈程度提高；升温速率增加，峰位高度降低，峰位后移。延长球磨时间，粉末粒径减小，粉粒之间的接触面积增加，利于反应进行，并使反应峰的尖锐程度提高，试样收缩倾向增大。提高加热温度,试样收缩加剧。24307
- 上一篇：反应型含SiP阻燃剂合成及其PU硬泡研究
- 下一篇：化学共沉淀法制备YAl3(BO3)4：Eu3+荧光粉
关键词 钛基复合材料 原位反应法 DSC分析
毕业设计说明书（毕业论文）外文摘要
Title Analysis of Ti-B4C System Titanium Matrix Composite Synthesed by In-situ Method
Abstract
This paper is about Al-Ti-B2O3 and Ti-B4C system titanium matrix composites which were successfully synthesized by the in-situ synthesizing method. Then, I analyzed the reaction process and the reaction resulted by some analyzing technique such as the photo of metallographic, XRD analysis and DSC analysis. The results indicate that the reactions in the two systems can be carried out spontaneously. The final products of Al-Ti-B2O3 system are Al2O3 and TiC enhancement based on titanium while the Ti-B4C system produces Al2O3 and TiC enhancement. We can also conclude that when there are more enhancements in the system, the reaction will act more dramatically. The differences in heating rate and milling time also have some influence on the reaction. When the heating rate is increased, the heat inside cannot be transmitted, so the reaction is insufficient. The height of the DSC peak thus reduces and its position moves backwards. The longer the milling time is, the smaller the diameter of the powder particles will be. So the contact area between the powder particles will increase, the reaction between them is relatively more intense and obvious. The sintering shrinkage of the sample increases when the milling time and the heating temperature increases.
Keywords titanium matrix composite in-situ synthesis
difference scanning calorimetric analysis
目次
1. 绪论 1
1.1 DSC（差热法） 1
1.2 原位合成技术 3
1.2.1 前言 3
1.2.2 表面原位复合 3
1.2.2.1 原位高能束表面熔覆法 3
1.2.2.2 原位反应喷射沉积法:RPS(Reactive Plasma Spraying) 3
1.2.2.3 原位铸造烧结法 4
1.2.3 整体原位复合 4
1.2.3.1 原位粉末烧结 4
1.2.3.2 原位自蔓延反应合成：SHS(self-propagating hight-temperature synthesis) 4
1.2.3.3 原位等离子体合成：PSM (plasma synthesis method) 5
1.2.3.4 原位反应铸造法 5
1.2.4 原位合成的反应机制 5
1.2.5 原位合成的发展方向 5
1.3 本课题的研究目的及内容 6
2.实验 6
2.1 实验原料 6
2.2 实验设备 7
2.3 实验内容 7
3. XRD、SEM分析反应 10
3.1 Ti-B4C反应体系 10
3.2 Al-Ti-B2O3反应体系 12
4. DSC分析 13
4.1 增强相体积分数对DSC的影响 14
4.2 升温速率对DSC的影响 15
4.3 球磨时间对DSC的影响 17
4.3.1 Ti-B4C反应体系 17
4.3.2 Al-Ti-B2O3 反应体系 17
5. 烧结收缩 19
结 论 20
-
以天工电炉粉尘高温固相法合成铁酸锌研究
-
中红外POBC多晶粉的合成与性能研究
-
2-丙烯酸甲氧基乙酯共聚物的合成与性能研究
-
2-甲氧基聚乙二醇丙烯酸酯...
-
三维氮掺杂石墨烯的合成与表征
-
碳包硫化亚铁纳米颗粒的合成及在锂电上应用
-
改性无水磷酸铁的合成技术研究
中国传统元素在游戏角色...
高警觉工作人群的元情绪...
巴金《激流三部曲》高觉新的悲剧命运
C++最短路径算法研究和程序设计
NFC协议物理层的软件实现+文献综述
江苏省某高中学生体质现状的调查研究
现代简约美式风格在室内家装中的运用
上市公司股权结构对经营绩效的影响研究
浅析中国古代宗法制度
g-C3N4光催化剂的制备和光催化性能研究