摘要：成核剂作为一种重要的助剂，对材料的机械性能有着显著的改变。本论文通过拉伸性能，三点弯曲性能，冲击性能等研究了PNA012对玻纤增强尼龙6力学性能的影响。我们借助XRD、DSC分析研究了PNA012对玻纤增强尼龙6结晶性能的影响。加入PNA012后，玻纤PA6的拉伸强度下降，当PNA012含量为0.7wt%时，拉伸强度由116.75MPa降到108.16Mpa，与玻纤增强尼龙6相比，下降幅度为7.36%。加入PNA012之后，玻纤PA6的断裂伸长率下降，当PNA012含量为0.5wt%时，断裂伸长率由4.71%下降到3.94%，下降幅度为0.77%。加入PNA012之后，玻纤PA6的冲击强度由8.86MPa下降到7.15MPa。玻纤PA6的弯曲模量随PNA012含量的增多而增强，弯曲模量由7441.18MPa上升到8011.22MPa。加入PNA012之后，玻纤PA6的热变形温度下降，热变形温度由189.17℃到181.40℃。通过XRD对比，发现未加入PNA012之前，玻纤PA6中α相占主导地位，加入PNA012之后，γ相占主导地位，当PNA012含量为0.5wt%时，γ相占98.30%。DSC结果显示，成核剂的加入使得结晶度增大，在成核剂含量0.7wt%的时候，达到最大值20.74%。5536
- 上一篇：Ni-γ-Fe2O3/SiO2复合镀层的制备工艺+文献综述
- 下一篇：CNTs/TPU复合材料的制备与性能研究
关键词：尼龙6；成核剂；力学性能；结晶性能
Effect of Nucleating Agent on Crystallization and Mechanical Properties of Glass Fiber Reinforced Nylon 6
Abstract: As a kind of important additives, nucleating agent has a significant change on material mechanical properties. Based on the tensile properties，Three-point bend performance, and impact properties etc, the thesis studied on the mechanical properties of glass fiber reinforced nylon 6.We analyze the crystallization properties of glass fiber reinforced nylon 6 affected of PNA012 by means of XRD, DSC. After adding PNA012，We find that the tensile strength of the glass fiber PA6 declines, when the content of PNA012 is 0.7 wt %,the tensile strength down from 116.75 MPa to 108.16 MPa, compared with glass fiber reinforced nylon 6, the descend range is 7.36%.After adding PNA012,glass fiber PA6 elongation at break declines, when the content of PNA012 is 0.5 wt %,elongation at break down from 4.71% to 3.94%,the descend range is 0.77%.After adding PNA012, the impact strength of glass fiber PA6 drops from 8.86 MPa to 7.15 MPa, Glass fiber bending modulus of PA6 enhanced along with the increase of the content of PNA012, rises from 7441.18 MPa to 8011.22 MPa. After joining PNA012, thermal deformation temperature of glass fiber PA6 drops from 189.17℃ to 181.40℃.By comparing the data of XRD, we find α phase is dominant in glass fiber PA6 without PNA012, after joining PNA012, γ phase dominate. When the content of PNA012 is 0.5 wt %, γ phase accounts for 98.30%.DSC results show that the adding of nucleating agent makes the crystallinity increase, when the content of nucleating agent is 0.7 wt %, the maximum rise to 20.74%.
Keywords：Nylon6；Nucleating agent；Mechanical properties Crystallization behavior；
目 录
1 绪论 1
1.1 引言 1
1.2 聚酰胺发展历史 1
1.3 成核剂的研究与展望 2
1.3.1 成核剂定义 2
1.3.2 成核剂的作用 2
1.3.3 成核剂的用量 3
1.4 PA的成核机理 3
1.4.1 PA的成核条件 4
1.4.2 PA成核剂的应用效果 4
1.5 成核剂的常用种类 4
1.6 课题研究目的和意义 8
1.6.1 研究目的 8
1.6.2 研究意义 8
2 实验部分 9
2.1 实验原料 9
2.2 实验设备 9
2.3 PA6与成核剂PNA012共混 9
2.4 玻纤增强PA6的注塑成型 10
2.5 玻纤增强尼龙6的各项机械性能测试 10
-
不同链长聚二甲基硅氧烷...
-
稀土元素Dy对合金涂层结构与高温性能的影响
-
金属氧化物对g-C3N4/TiO2复合...
-
Bi含量对Sn-Bi/Cu界面化合物生长影响的研究
-
粉料尺寸对BaTiO3陶瓷烧结工艺研究
-
工艺参数对高硅铝合金CMT组织与性能的影响
-
表面预处理对水下药芯电弧切割的影响
NFC协议物理层的软件实现+文献综述
江苏省某高中学生体质现状的调查研究
g-C3N4光催化剂的制备和光催化性能研究
现代简约美式风格在室内家装中的运用
中国传统元素在游戏角色...
高警觉工作人群的元情绪...
上市公司股权结构对经营绩效的影响研究
巴金《激流三部曲》高觉新的悲剧命运
浅析中国古代宗法制度
C++最短路径算法研究和程序设计