摘要：基于对传统力学的理论的金属板材弯曲变形计算；通过理论计算分析综合评述强烈变形（Severe Plastic Deformation）机理和变形方法的特点以及应用前景；对晶粒分析与轧制方法相结合的强烈变形对金属材料组织（晶粒）变化影响。从而确定使用反复弯曲的方法进行试验，进一步分析轧制与不同曲率半径的反复弯曲变形IF钢的组织（晶粒）与性能变化的影响。同时，结合热处理工艺，进一步分析IF钢轧弯组合变形对其组织与性能变化的影响，取得试验结论。57959

毕业论文关键字：IF钢；金相显微镜；维氏硬度计；轧弯组合；晶粒细化

Effect of bending deformation on Microstructure and properties of IF steel

Abstract: Based on the theory of traditional mechanical sheet metal bending deformation calculation. Through theoretical calculation analysis of a comprehensive review of intense deformation (severe plastic deformation mechanism and deformation characteristics and application prospect; on grain analysis and rolling method combined with the strong deformation of metal micro structure (grain) change. In order to determine the influence of the micro structure (grain) and the properties of the IF steel with different curvature radius, the experiment was carried out by using the method of repeated bending. At the same time, combined with the heat treatment process, the influence of deformation on the micro structure and properties of IF steel rolling and bending combination was further analyzed.

Key word: IF steel ;Optical microscope; Vivtorinox hardness tester; rolling and bending combination; grain refinement

 目录

1绪论 1

1.1 研究目的 1

1.2 研究意义 1

1.3 研究背景 2

1.4 国内外的生产状况 3

1.4.1  IF钢轧制技术的发展 3

1.4.2  IF钢工艺生产要点 3

1.4.3  未来我国IF钢的发展 4

1.5 改善金属材料组织（晶粒）与性能的研究概况 4

1.5.1 抗弯组合变形的研究 5

1.5.2 强烈变形在高强度IF钢的研究 5

1.5.4 强烈塑性变形的方法 6

1.5.5  抗弯组合变形在IF钢中的研究 7

1.5.6  多点弯曲中的成形的应用 8

1.5.7 轧弯组合变形改善金属材料组织性能的意义 8

2 分析 9

2.1 研究方案与技术路线 9

2.1.1 预先准备方案 9

2.1.2 实际操作路线 9

2.2 实验仪器及材料 9

2.2.1 实验设备图 10

2.2.2 试样图 11

2.2.3 金相观察设备图 12

2.3 热处理制度 12

2.4 实验测试方法 13

2.4.1 金相组织观察 13

2.5 弯曲设计测试 14

2.5.1 晶粒尺寸测定 14

3 设计 15

3.1 引言