摘要染料废水水污染严重, 成分复杂, 一直是工业废水处理的难点。纳米二氧化锰具有较大的比表面积和活性点，可以催化降解染料分子，广泛应用于催化、污水净化等领域。本文采用水热合成法，用KMnO4和MnSO4·H2O制备了不同形貌的纳米MnO2。用XRD和SEM对样品进行了表征，通过MnO2对亚甲基蓝的降解实验测试了其光催化性能。结果表明MnO2对亚甲基蓝溶液有很好的催化降解作用，具有很好的光催化性能。67478

毕业论文主关键词：  纳米二氧化锰  水热合成  亚甲基蓝  光催化

毕业设计说明书（论文）外文摘要

Title:   Hydrothemal Synthesis,Characterization and Properties of MnO2  Nanostructures               

Abstract

Serious wastewater pollution, complex composition, has been the difficulty of industrial wastewater treatment.Manganese dioxide nanostructures has a larger surface area and active sites can catalyze the degradation of dye molecules, are widely used in catalysis, water purification and other fields.In this paper, we hydrothermal synthesised MnO2 of different morphologies by using KMnO4 and MnSO4·H2O .We characterized the samples By XRD and SEM.We tested its photocatalytic performance By the degradation of methylene blue experiments. The results showed that MnO2 having a good catalytic degradation to methylene blue. MnO2 nanostructures have good photocatalytic properties.

Keywords:  MnO2Nanostructures  HydroccthemalSynthesis  MethyleneBlue  Photocatalytic

目 次

第一章 绪论 1

1.1 光催化反应 1

1.2 二氧化锰的结构和分类 2

1.3 纳米二氧化锰材料的制备 5

1.4 本课题的研究背景及意义 8

第二章 测试方法与原理 9

2.1  X 射线衍射分析(XRD) 9

2.2  扫描电子显微分析(SEM) 9

2.3  透射电子显微分析(TEM) 9

2.4  比表面积分析(BET) 10

2.5  UV-vis分析 10

第三章 纳米二氧化锰的水热合成及其光催化性能 11

3.1 样品的制备 11

3.2实验过程 13

3.3 光催化测试 16

结  论 18

致  谢 19

参考文献 20

第一章 绪论

纳米材料是指晶粒尺寸为 0.l~100nm 的超细材料。纳米材料具有一系列特性，如量子尺寸效应、小尺寸效应、表面效应和量子隧道效应，因而带来光、电、磁、热、声乃至超导等方面与宏观特性显著不同，使得它们在磁性材料、电子材料、光学材料、催化剂等方面已经得到成功的应用。故近年来人们在对二氧化锰纳米材料的制备和应用方面作了诸多研究。

染料废水水污染严重, 成分复杂, 一直是工业废水处理的难点。通常采用物理方法和氧化技术去除染料废水中有机污染物。但物理方法没有破坏有机物污染物分子本身, 需要进一步的后续的处理, 可能会造成二次污染。Fenton氧化法和TiO2光催化反应由于受到条件限制, 很难被推广应用。纳米二氧化锰具有较大的比表面积和活性点，可以催化降解染料分子，广泛应用于催化、分子筛、超级电容器、锂离子电池、污水净化等领域。