摘要采用模板法。以PLLA、PEO、TTIP为原料，控制PLLA与PEO两者的比例不变，仅改变TTIP的量。设置原料配比分别为1:1:0。5，1:1:1，1:1:2。先配制PLLA/PEO/TTIP溶液再对其成膜；然后对膜进行退火处理后经DSC测试和POM观察，分析可知POM图像上出现的是PEO大球晶，而PLLA与PEO则发生相互作用；最后对膜进行煅烧处理后经SEM探究和XRD测试，分析可知最终退火煅烧后的产物是纯的锐钛矿型TiO2，拥有二维的多孔TiO2片层结构，且三组中的最佳原料配比为1:1:1。74508

Abstract：Using the template method。 Put the PLLA, PEO, TTIP as raw materials, control the ratio of both PEO and PLLA unchanged, but only change the mass of TTIP。 Set the ratio of raw materials as 1:1:0。5, 1:1:1, 1:1:2 respectively。 First of all, PLLA/PEO/TTIP solution was prepared to form films。 Then after annealing treatment was carried out on the films, the large PEO spherulites were found through the DSC test and POM, but PLLA interact with PEO。 Finally, after calcination treatments was carried out on the films, the analysis results of SEM and XRD show that the final annealing and calcined product is pure anatase TiO2,which possessed two-dimensional and porous TiO2 lamellar structure。 The optimum proportion of the three groups is 1:1:1。

毕业论文关键词：TiO2薄膜；模板法；TiO2片层结构

Keywords:  Tio2 thin film; Template method; TiO2 lamellar structure

目    录

1 引言 5

1。1  纳米材料 5

1。2  多孔材料 6

1。3  TiO2的晶体结构 6

1。4  TiO2的性质与应用 7

1。4。1 光催化 7

1。4。2 抗菌作用 8

1。4。3 颜色效应 8

1。4。4 防雾自洁 8

1。4。5 传感器方面的应用 9

1。5  多孔TiO2薄膜的制备方法 9

1。5。1 化学气相沉积（CVD）法 9

1。5。2 溶胶-凝胶(Sol-Gel)法 10

1。5。3 模板法 10

2 实验部分 12

2。1  实验原料及设备 12

2。1。1  实验原料 12

2。1。2  实验设备 12

2。2  实验步骤 12

2。2。1  PLLA/PEO/TTIP溶液的配制 12

2。2。2  溶液成膜 12

2。2。3  薄膜的退火处理 13

2。2。4  薄膜的煅烧处理 13

2。3  实验的表征方法 14

2。3。1  差示扫描量热仪(DSC) 14

2。3。2  偏光显微镜（POM） 14

2。3。3  扫描电子显微镜(SEM) 14

2。3。4  X射线衍射(XRD) 14

3 结果与讨论 15

3。1  差示扫描量热仪(DSC)分析 15

3。2  偏光显微镜（POM）下薄膜的形貌特征