摘要本文主要概述了导电铝复合排的研究背景、国内外的研究现状，以及钎焊的相关知 识，通过测试钎料、钎剂的 DTA 曲线，来选择合适的钎焊钎料、钎剂，用金相显微镜 观察钎焊后焊缝的金相显微图片，分析钎焊后的样品。通过本次研究，我们选择了 Zn85Al15 作为实验的钎料，选择了国外的氟铝酸铯作为实验的钎剂，而且通过对火焰钎 焊和弧焊的焊缝进行金相分析，发现火焰钎焊的样品母材和钎料结合紧密，而且产生的 缺陷也比较少，通过钎焊连接技术是可以将导电铝复合排很好地连接在一起。81124

毕业论文关键词：导电铝复合排；钎焊 ；钎料；金相分析

Abstract This paper provides an overview of research background of the aluminum conductor composite row ,the domestic and foreign research status, and soldering related knowledge, through DTA curve test solder and fluxes,and observed brazing weld Metallographic microstructure pictures, to select suitable brazing filler metal and flux, and brazing analysis of samples。Through this study, we choose the Zn85Al15 as the brazing filler metal, choose the foreign aluminum fluoride acid cesium as experimental flux, and through the flame brazing and welding weld metallographic analysis, found that flame brazing samples of base metal and filler metal closely, and defects of relatively small, the brazing technology is can be conductive aluminum composite exhaust well connected together。

Key words: conductive aluminum composite; brazing; brazing filler metal  ; metallographic analysis

目 录

第一章 绪论 1

1。1 研究背景和意义 1

1。2 国内外研究现状 1

1。3 本文研究内容和方法 2

1。3。1 研究内容 2

1。3。2 研究方法 2

1。4 导电铝复合排 2

1。4。1 导电铝复合排的介绍 2

1。4。2 导电铝复合排的优点 3

1。5 钎焊 3

1。5。1 钎焊的简介和优点 3

1。5。2 钎焊过程 4

1。5。3 钎焊的特点 4

1。5。4 钎焊的分类 5

1。5。5 本次实验所采用的火焰钎焊 5

1。5。6 钎焊的发展及现状 6

1。6 钎料和钎剂 7

1。6。1 钎料的简介 7

1。6。2、钎料的性能要求 7

1。6。3、钎剂的基本要求 7

1。7 导电铝复合排的钎焊研究 8

1。7。1 铜与铜的钎焊 8

1。7。2 铝与铝的钎焊