摘要：本文以四氯化锡晶体（SnCl4·5H2O）和氢氧化钠固体（NaOH）为原料，通过水 热合成法，以 Zn 片为基底制备 SnO2 纳米棒阵列膜；通过改变反应温度和反应时间，探究 制备 SnO2 纳米棒阵列膜的最佳条件；用扫描电子显微镜（SEM）对其结构进行表征，并以 酸性大红 GR 为目标染料，在汞灯的照射下，利用紫外分光光度计探究 SnO2 纳米棒阵列膜 的光催化性能。结果表明，200℃和 12h 为制备 SnO2 纳米棒的最佳条件，在 120min 内降解 酸性大红 GR 的降解率达 69。7%。从 SEM 图可以看出其直径约为 18nm，长度约为 50nm。 Abstract：Based on zinc foils,using stannic chloride pentahydrate and sodium hydroxide as raw materials,SnO2 nanorod array films are prepared by hydrothermal method。By changing reaction temperature and time,the optimum condition of preparation was explored。Its structure was characterized by scanning electron microscope。Under the mercury lamp ,using acid brilliant scarlet GR as targets,photocatalytic performance of SnO2 nanorod array films are explored by ultraviolet spectrophotometer。The result shows, 200℃and 12hours is the best condition, acid brilliant scarlet GR has been degraded to the rate of 69。7 % within 120 minutes。in addition，its diameter is 18nm and its length is 50 nm。源Y于U优I尔O论P文W网wwW.yOueRw.com 原文+QQ75201-8766

毕业论文关键词：水热法，SnO2 纳米棒阵列膜，光催化，酸性大红 GR89078

Keyword: hydrothermal method,SnO2 nanorod array films, photocatalysis, acid brilliant scarlet GR

目录

1。  引言 4

1。1  研究背景 4

1。2 研究意义 4

1。3  研究内容及要解决的问题 4

1。3。1 SnO2 纳米棒阵列膜的制备 4

1。3。2  探究制备的最佳反应温度和时间 4

1。3。3。  光催化实验 5

1。3。4  电镜表征分析 5

1。4  国内外研究现状 5

1。4。1 国内研究现状 5

1。4。2 国外研究现状 5

2。  纳米 SnO2 的概述 5

2。1 SnO2 的基本来自优Q尔W论E文R网wWw.YouERw.com 加QQ75201.8766 性质 5

2。2 SnO2 纳米列阵的制备方法 6

2。2 SnO2 的光催化原理 6

3。实验部分 7

3。1  实验试剂 7

3。2 实验仪器 7

3。3 实验内容 7

3。3。1 SnO₂纳米棒状阵列膜的合成 7

3。3。2 产物表征 8

3。3。3  光催化性能测试 8

3。3。4  数据处理 8

3。4  结果与分析 8

3。4。1  扫描电镜（SEM）分析 8

3。4。2 SnO2 纳米阵列的光催化性能 11

4。结论 13

参考文献 13

1。  引言

1。1  研究背景

随着工业的发展，中国面临着严峻的水污染现状，所以如何治理水污染就成了人们所关 注的焦点。目前我们主要有两种方法来处理污水，分别是物理处理法和化学处理法，发展到 后期，人们把物理方法和化学方法相结合，在处理中同时运用到了物理变化和化学变化，比 如膜处理技术就是典型的代表[1-2]。但是以上方法具有净化率低下、应用范围狭窄等缺陷， 因此一些新兴污水处理技术的出现与研究是必然的。目前科学家们已经发现了一些新的方法， 比如纳米材料光催化法就是其中一个。我们可以利用金属氧化物纳米材料如 TiO2、ZnO 和 SnO2 等作为催化剂，在光照条件下，污水中的有机物会被降解为二氧化碳和水等无毒无害 的物质[3]。论文网