摘    要二氧化钼纳米材料具有良好的光催化性能。光催化反应可以将光能转化为化学能，降解水和空气中的各种污染物，所以光催化在环境污染治理和新能源开发方面具备巨大的潜力。本文分析了稀土掺杂钼氧化物的国内外合成现状，经过对比后设计了一种新的合成方法。称取一定质量的原料配成溶液，将所需溶液倒在烧杯中,用磁力搅拌器搅拌20分钟,使它们充分混合。然后将混合溶液转移至高压反应釜中，在180℃条件下加热12小时。冷却至室温后，对混合溶液进行离心分离，并用乙醇清洗沉淀，然后在60℃条件下烘干6小时。这样就制备得到了稀土掺杂MoO2。最后对其进行XRD测试，光催化性能测试、透射电镜测试。89616

Abstract The molybdenum dioxide nanomaterials have good photocatalytic performance。 Photocatalytic reactions can convert light energy into chemical energy, degrade water and various pollutants in the air, so photocatalytic has great potential in environmental pollution control and new energy development。 This paper analyzes the synthesis of rare earth doped molybdenum oxide at home and abroad, and then a new synthetic method is designed。Weigh the raw material into a certain amount of the solution, pour the desired solution in a beaker and stir for 20 minutes with a magnetic stirrer to allow them to mix well。 The mixed solution was then transferred to a high pressure reactor and heated at 180 ℃ for 12 hours。 After cooling to room temperature, the mixed solution was centrifuged and the precipitate was washed with ethanol and then dried at 60 ℃ for 6 hours。 In this way, rare earth doped MoO2 was prepared。 In the end, we take the X-ray diffraction test, photocatalytic performance test, transmission electron microscopy test。

毕业论文关键词：稀土； 二氧化钼； 水热合成；光催化

Keyword: rare earth；molybdenum dioxide； hydrothermal synthesis；photocatalysis

目    录

1 引言 5

1。1 研究背景 5

1。2 国内外研究现状 5

1。2。1 二氧化钼 5

1。2。2 稀土掺杂方法 6

1。2。3 光催化机理 7

1。3 研究意义 8

2 实验部分 8

2。1 反应机理 8

2。2 实验材料与源Q于W优E尔A论S文R网wwW.yOueRw.com 原文+QQ75201,8766 仪器设备 8

2。2。1 实验材料 8

2。2。2 仪器设备 8

2。3 实验方法 9

3 结果与讨论 10

3。1 XRD测试 10

3。2 光催化性能测试 11

3。2。1 实验方法 11

3。2。2 数据分析 12

3。2。3 动力学研究 14

3。3 透射电镜测试 15

4 结论 17

参考文献 18