摘   要 本文通过PVC在增塑剂中的溶解温度、增塑剂吸收量、以及PVC制品软硬度、迁移率等性能方面的测试，考察了新型环保增塑剂环己烷二甲酸二丁酯(氢化邻苯二甲酸二丁酯)及其与DOTP复配对PVC的增塑性能。溶解温度与吸收量的结果表明，环己烷二甲酸二丁酯的塑化性能稍不及邻苯二甲酸二丁酯。DBP的PVC制品软硬度及迁移率均高于HDBP相应PVC制品。85310

Abstract

In this paper, the dissolution temperature of PVC in plasticizer, the amount of plasticizer absorbed, and the softness and mobility of PVC products were tested。 The effects of environmental protection plasticizer cyclohexanedicarboxylic acid dibutyl ester Dibutyl phthalate) and its synergistic properties with DOTP for PVC。 The results of dissolution temperature and absorption showed that the plasticity of dibutyl cyclohexanate was less than that of dibutyl phthalate。 DBP PVC products, hardness and mobility are higher than HDBP corresponding PVC products。

毕业论文关键词:1、2-环己烷二甲酸二丁酯；聚氯乙烯；增塑性能

Keyword：dibutyl hexahydrophthalate；Polyvinyl chloride；Plasticizing performance

目录

第一章  绪论 4

1。1引言 4

1。2PVC的概述 4

1。3增塑剂的概述 5

1。3。1增塑剂源Q于W优H尔J论K文M网WwW.youeRw.com 原文+QQ75201.,8766 的分类 5

1。3。2增塑剂的应用 6

1。4国内外的研究现状 6

        1。4。1国内的研究现状 7

        1。4。2国外的研究现状。 7

第二章 实验部分 7

2。1实验原料和试剂 8

2。2实验仪器及来源 8

2。31、2-环己烷二甲酸二丁酯增塑性能评价 8

2。3。1溶解温度 8

2。3。2增塑剂吸收量与温度、时间的关系 8

2。3。3PVC制品软硬度 8

        2。3。4增塑剂迁移性。。9

        2。3。5增塑剂复配。。9

第三章  实验结果讨论 10

3。1评价增塑剂与PVC相互作用力 10

3。2评价增塑剂吸收快慢与温度、时间的关系 10

3。3PVC制品软硬度 11

3。4增塑剂迁移性 12

3。5增塑剂复配。。。12

第四章  结论 13

参考文献 16

致谢 17

第一章绪论

1。1引言

PVC具有抗腐蚀、耐热性，难以燃烧，绝缘性好的特性，是世界上产量较高的通用塑料，在工业、农业、日用品商品包装上均有较广泛的应用。但PVC的内聚力比较大，在加工过程中必须添加增塑剂，以优化其加工性能。增塑剂是一种增加材料柔软性的添加剂，在塑料、水泥、混凝土、墙壁材料中以广泛添加。同一种增塑剂加入不同的材料中会有不同的功能。来自优W尔Y论W文C网WWw.YoueRw.com 加QQ7520,18766