摘 要：本文通过相转化法制备非对称膜，将聚甲基丙烯酸-N,N-二甲基氨基乙酯（PDMAEMA）添加到聚偏氟乙烯（PVDF）超滤膜中进行改性，通过改变凝固浴的pH值来制备不同的超滤膜，考察了凝固浴的不同pH值对PVDF膜微观结构、孔径、纯水通量、孔隙率的影响。实验结果表明，凝固浴pH值的变化对膜有一定影响，而对膜的晶体结构基本没有影响。当凝固浴为酸性条件时，膜的晶粒较多、较大且缺陷孔较少，热稳定性和纯水通量最高。通过孔径、孔隙率分析可知，凝固浴pH值的改变对膜孔径及孔隙率大小影响不大。85721

毕业论文关键词：PVDF超滤膜，膜改性，凝胶条件，结构表征 

Abstract：In this paper, asymmetric films were prepared by phase inversion method。 Poly [2- (N, N- dimethyl amino) - ethyl methacrylate] (PDMAEMA) was added to the polyvinylidene fluoride (PVDF) ultrafiltration membrane。 Different ultrafiltration membranes were prepared by varying the pH of the coagulation bath。 The effects of different pH values on the microstructure, pore size, pure water flux and porosity of PVDF membrane were investigated。 The experimental results showed that the change of the pH value of the coagulation bath had some influence on the membrane。 But it had no effect on the crystal structure of the membrane。 Under the acidic condition, membrane grain was more, larger and less defective。 The thermal stability and the pure water flux of the membrane was the highest。 Through the analysis of pore size and porosity, it was found that the change of pH value of coagulation bath had little effect on membrane pore size and porosity。

Keywords：PVDF ultrafiltration membrane, membrane modification, gel condition, structural characterization

目   录

1  引言 4

1。1  超滤技术简介 4

1。2  超滤的膜材料 4

1。3  PVDF超滤膜的制备与改性 5

1。4  主要研究内容 6

2  实验部分 6

2。1  实验药品及仪器 6

2。2  聚偏氟乙烯超滤膜的制备 8

2。3  膜的表征 9

2。4  孔径测量 9

2。5  纯水通量的测试 9

2。6  孔隙率的测试 10

3  结果与讨论 10

3。1  红外光谱分析 10

3。2  X射线衍射分析 11

3。3  扫描电镜分析 11

3。4  热稳定性分析 12

3。5  孔径分析 13

3。6  纯水通量分析 14

3。7  孔隙率分析 15

结  论 17

参 考 文 献 18

致  谢 20

1  引言

1。1  超滤技术简介

1。1。1  超滤原理

超滤是以超滤膜两侧的压力差为驱动力，利用筛除机理去除原液中的杂质，在一定的压力下，当原液透过超滤膜时，超滤膜表面分布的许多微孔把原液中的大分子及杂质截留在膜的一侧，而小于膜表面微孔的小分子被通过。从而实现对原液的分离和净化[1,2]。