摘要：本文以多璧纳米碳管（MWCNT）为载体合成了MnO2@MWCNT复合材料，采用扫描电镜、能谱分析仪、红外分光仪、粉末衍射仪、比表面、孔径分布分析仪及交流阻抗谱对合成的材料进行了表征，在1M硫酸钠溶液中，采用恒电流充放电技术及循环伏安法对MnO2@MWCNT组装的电容电极进行了测定，为了获得的较好的比电容和稳定性获得了MnO2：MWCNT最佳质量比。91075

毕业论文关键词：MnO2,MWCNT,超级电容器

Abstract：In this paper the MnO2@MWCNT nanocomposites have been successfully synthesized using Multi walled carbon nanotubes as a support for the supercapacitor, the as-prepared nanocomposites was characterized by scanning electron microscopy, energy dispersive spectrometer, infrared spectrometer, X-ray diffractometer, surface area and pore size analyzers, and electrochemical impede。 The cyclic voltammetry and galvanostatic charge/discharge were performed for MnO2@MWCNT in 1 M Na2SO4 aqueous solutions。 The best mass rate of MnO2: MWCNT was obtained for the higher specific capacitance and long life time。源G于J优L尔V论N文M网WwW.youeRw.com 原文+QQ75201`8766

Keywords：MnO2, MWCNT, supercapacitor

目  录

1  前言 3

2  实验部分 3

2。1  试剂与器材 3

2。2  仪器 3

2。3  MNO2@MWCNT的合成 4

3  结果与讨论 4

3。1  比表面及孔径分布 4

3。2  MWCNT及MNO2@MWCNT电镜分析 5

3。3  MWCNT及MNO2@MWCNTXRD 7

3。4  MNO2@MWCNTIR 8

3。5  MNO2@MWCNT超级电容器性能 9

3。6  MNO2@MWCNT交流阻抗分析 13

4  结论 15

参考文献： 16

致谢 17

1  前言

超级电容器是一种新型储能元件,具有更高的能量密度，具有瞬间释放特大电流、充放电效率高、循环寿命长等特点。在信息技术、移动通信、电动汽车、消费电子、航空航天和国防科技等领域具有重要和广阔的应用前景。氧化锰资源广泛，价格低廉，环境友善，具有多种氧化价态，被广泛用作电池电极材料和氧化催化剂材料[ - ]。论文网

金属氧化物在电极/电解液界面产生的赝电容远大于碳材料表面的双电层电容，因而成为近年来研究的热点。目前已应用的金属氧化物有：IrO2,SnO2,V2O5, MnOx,NiO,Co2O3,RuO2,及 MoOx等。其中锰的氧化物资源丰富、而受到关注。氧化锰用作超级电容器的电极材料是近年来才发展起来的，其在中性电解液中表现出良好的电容特性，且电位窗口较宽，被认为是极具发展潜力的一种电极材料[5-9]。研究者目前正在采取多种方法法制备具有良好电容特性的超级电容器。

MWCNT化学性质稳定，具有较大的比表面积及较高的反应活性，广泛用于吸附剂、催化剂、粘胶剂、催化剂载体。

本文以高锰酸钾为氧化剂，硫酸锰为还原剂，以MWCNT为载体，合成了MnO2@MWCNT纳米颗粒，研究其超级电化学行为。

2  实验部分

2。1  试剂与器材

KMnO4，无水Na2SO4，MnSO4无水乙醇，去离子水，70%（w/w）水合肼。1×1cm2铂网。所用试剂均为分析纯。