摘  要：本论文主要采用预聚体分散法，以二苯基甲烷二异氰酸酯（MDI）和聚醚多元醇（PPG2000）为原料，二羟甲基丙酸（DMPA）为亲水扩链剂，合成预聚体。加入三乙胺中和后，加水乳化制得水性聚氨酯乳液，然后通过改变亲水性试剂DMPA的含量测定对其粘性的影响，改变反应温度其粘性的影响，改变三甲基磷酸酯（TMP）含量对其粘性的影响。91191

毕业论文关 键 词：水性聚氨酯胶粘剂，二羟甲基丙酸，预聚体，胶黏剂

Abstract：In this paper, the prepolymer dispersion method was used, and diphenylmethane diisocyanate (MDI) and polyether polyol (PPG2000) were used as raw materials, dimethylol propionic acid (DMPA) was used as hydrophilic chain extender。 The addition of triethylamine was added to the aqueous solution and then emulsified to obtain an aqueous polyurethane emulsion which was then subjected to a change in the content of the hydrophilic reagent DMPA to determine its effect on its viscosity, changing the reaction temperature of its viscosity, changing the trimethyl phosphate TMP) on its viscosity。源G于J优L尔V论N文M网WwW.youeRw.com 原文+QQ75201`8766

Keywords：Waterborne polyurethane adhesives,  dimethylol propionic acid,  prepolymers, adhesives

目   录

1  前 言 5

2 实验部分 5

2。1 反应方程式 5

2。1。1 实验试剂 6

2。1。2 实验仪器 6

2。2 实验原理 6

2。2。1 WPU制备基本原理 6

2。3 实验步骤 7

2。3。1聚氨酯胶黏剂乳液的制备 7

2。3。2胶膜的制备 7

2。4 实验测试与表征 7

2。4。1 傅立叶红外光谱表征 7

2。4。2 热失重测试 7

2。4。3 耐水性能测试 7

2。4。4 乳液固含量的测定 8

2。4。5 贮存稳定性的测定 8

2。4。6 胶黏剂合成路线 8

3 结果与讨论 9

3。1 反应比例的影响 9

3。2 反应温度的影响 10

3。3  TMP含量对水性聚氨酯胶乳及胶膜性能的影响 11

结  论 13

参 考 文 献 14

致谢 15

1  前 言

在当前的日常生活中随着人们的安全和环保意识的加强,水性聚氨酯胶黏剂的研究得以迅速发展。水性聚氨酯胶黏剂是指水和聚氨酯互相融合或者聚氨酯分散在水中而形成的胶黏剂,与传统的溶剂型的聚氨酯胶黏剂相比具有无溶剂、无污染、成膜性好、粘接力强等优点。90年代以后后已经逐渐开始在厨房用品制造、复合薄膜制造、鞋底鞋帮粘接、服装加工等方面得到非常广泛的应用。但是因为传统聚氨酯胶黏剂中含有大量有机物质，对人的身体有毒害性，所以人们就对它进行研究和改性。现如今水性聚氨酯胶粘剂已经得到了很大的完善，它没有毒性，对人的身体也没有毒害性，而且它几乎可以遍及交通运输、建筑、机械、家具、电子设备、印刷、冶矿等众多的领域。