摘要：本文首先以异佛尔酮二异氰酸酯和甲基丙烯酸羟乙酯为原料合成半封端的聚合物，再由甲基丙烯酸、丙烯酸正丁脂、甲基丙烯酸羟乙酯和甲基丙烯酸十二氟庚酯合成含氟共聚物，进而合成含氟丙烯酸酯，最终通过相反转获得水性涂料。采用红外光谱等技术确定分子结构。反应过程中通过测定不同温度下-NCO含量随时间的变化，确定最佳的反应温度，其中合成半封端预聚物的最佳反应温度为45 ℃，而含氟甲基丙烯酸酯的最佳反应温度为70 ℃。改变甲基丙烯酸的用量考察其对乳液的影响，发现当甲基丙烯酸用量为5 %时，所得乳液稳定性较好，易于储存。通过对不同固含量的研究发现，30 %固含量不仅可以得到综合性能较好的乳液，而且还有不错的经济价值。84715

毕业论文关键词：甲基丙烯酸;紫外固化;水性;含氟;相反转

Waterborne UV-curable Flourinated Copolymer

Abstract: In this paper, the half-blocked polymer IPDI-HEMA was synthesized by using isophorone diisocyanate and hydroxyethyl methacrylate as a raw material, and the fluorine-containing copolymer was synthesized by n-butyl acrylate, methacrylate resin, hydroxythyl methacrylate and methacrylic acid ester, then fluorine-containing acrylate was synthesized, and finally the waterborne coating was prepared through phase inversion。 Molecular structure was determined by infrared spectroscopy。 In the experience, -NCO content was measured at different temperatures to determine the optimum reaction temperature of half-blocked polymer IPDI-HEMA was 45 ℃ and fluorine-containing acrylate was 70 ℃。 Studying the effects of different methacrylate content to emulsion, it was found that when the value was 5 %, the resulting emulsion was more stable and convenient to storage。 Through the study of different solid content, it was found that when the solid content was 30 %, the coating can not only get a better overall performance, but also a good economic value。

Key Words: Methacrylic acid; UV curing; Aqueous; Fluorine-containing; Phase inversion

目    录

摘  要 1

引  言 2

1 实验部分 3

1。1 实验试剂 3

1。2 实验仪器 3

1。3 实验过程 4

1。4 测试方法 6

2 结果与讨论 6

2。1 红外光谱 6

2。2 实验温度 7

2。3 甲基丙烯酸的用量 9

2。4 相反转 9

3 结  论 10

参考文献 11

致  谢 13

水性紫外光固化聚氨酯丙烯酸酯的合成

引  言

纯的丙烯酸乳液出现在上世纪50年代，但是由于价格昂贵而而使其应用受到限制。70年代以来由于环保法案的制定和大众环保意识的提高，传统涂料由于其中的有机化合物易挥发的问题而被人们抛弃，新型涂料的研发也日益受到人们的关注。水性紫外光固化聚氨酯丙烯酸酯涂料以其优异的性能脱颖而出。论文网

水性涂料优点很多，不仅可以提高产品的最终附着力，同时还解决了传统涂料不能兼顾硬度和柔韧度的问题。另外水性体系可以方便的调节涂料的流变性，更加方便获得极薄的涂层，适用于喷涂等涂布方式；其设备在清理的时候也十分方便；且水是安全廉价的介质，不易燃烧[1,2]。