摘    要在一定合成条件下，微孔磷酸盐分子筛无论在紫外还是可见光区都具有良好的光学透过性，而由于其自身孔道所提供的空间限制作用易于使客体物质形成有具有量子尺寸效应的微米粒子，这就使其成为发光材料的理想载体。本研究将微孔磷酸镍材料VSB-1与稀土元素相复合。88741

（1）采用水热法，通过对原料配比、溶液pH值、反应温度和反应时间等合成条件的控制，成功合成出微孔磷酸镍材料VSB-1。

（2）在合成VSB-1的基础上，掺杂不同摩尔比的Yb3+。

（3）使用XRD、扫描电镜等对所合成材料的结构、形貌等进行测试和表征。

（4）使用荧光光谱仪对所合成材料的发光性能进行研究。

Abstract Under the certain condition of synthesis, microporous phosphate molecular sieve have a good optical permeability in ultraviolet and visible light region。 And due to the spatial limitation provided by its own channels, it is easy to form the guest material with micron particles with quantum size effect。 This makes it an ideal vehicle for the luminescent material。 In this study, the microporous nickel phosphate material VSB-1 was compounded with rare earth elements 

(1) The microcrystalline nickel phosphate material VSB-1 was successfully synthesized by hydrothermal method, such as the ratio of raw materials, pH value, reaction temperature and reaction time。 

(2) On the basis of the synthesis of VSB-1, Yb3 + with different molar ratios was doped。

(3) The structure and morphology of the composites were tested and characterized by XRD, IR and SEM。 

(4) Fluorescence spectrometer is used to study the luminescence properties of synthetic material。

毕业论文关键词：稀土； 微孔材料；磷酸盐；发光性能

Keyword: rare earth；Microporous Materials； phosphate；Luminous properties 

1。前言4

1。1微孔材料的研究历程及其性质 4

1。1。1分子筛科学的研究过程 4

1。1。2微孔材料的性质和种类4

1。2 VSB系列分子筛的发展概述 5

1。3稀土元素的发光性质。5

1。4微孔材料在合成发光材料中的前景。6

2。实验部分 6

2。 1实验材料与仪器设备 6

2。1。1实验材料 6

2。1。2实验设备 6

2。2未掺杂VSB-1制备 6

2。3 Yb3+掺杂VSB-1制备 7

3。 结果与源Q于D优G尔X论V文Y网wwW.yOueRw.com 原文+QQ75201`8766 讨论 8

3。1 XRD测试 8

3。1。1  未掺杂VSB-1XRD测试 8

3。1。2  不同Yb3+掺杂比的VSB-1XRD测试 9

3。1。3  新增Yb3+掺杂比的VSB-1XRD测试。12

3。1。4  各摩尔浓度VSB-1XRD图的规律总结。15

3。2扫描电镜 15

3。3荧光光谱（346nm） 16

3。3。1  未掺杂VSB-1荧光光谱(346nm)。17

3。3。2  不同Yb3+掺杂比的VSB-1荧光光谱 18

3。3。3  掺杂不同比例的Yb3+的VSB-1荧光光谱比较。21

3。4 近红外发光光谱（NIR）。23

    3。4。1  未掺杂VSB-1近红外发光光谱23

    3。4。2  不同Yb3+掺杂比的VSB-1近红外发光光谱23