摘 要：水性聚氨酯（WPU）是一种新型以水为分散介质的聚氨酯体系，由于其无毒、环保、使用安全，已经引起国内外的广泛关注。本论文主要采用预聚体分散法，以二苯基甲烷二异氰酸酯（MDI）和聚丙二醇2000（PPG2000）为原料，二羟甲基丙酸（DMPA）为亲水扩链剂，合成预聚体，加入三乙胺中和后，加水乳化制得水性聚氨酯乳液。研究了-NCO/-OH比值的变化、TMP含量变化、-COOH在预聚体中的百分含量变化对水性聚氨酯胶黏剂性能的影响。91504

毕业论文关键词：水性聚氨酯，二羟甲基丙酸，预聚体，胶黏剂

Abstract：Waterborne polyurethane (WPU) is a new type of water as dispersion medium polyurethane system, Because WPU is non-toxic, environmentally friendly and safe, it has attracted widespread attention at home and abroad。 This thesis mainly adopt the chain polymerization method, with diphenyl methane diisocyanate (MDI) and poly propylene glycol 2000 (PPG2000) as raw material, with dihydroxy methyl propionic acid (DMPA) as hydrophilic chain extender, synthetic polymers, triethylamine neutralization, water emulsion was prepared waterborne polyurethane emulsion。 Effects of -NCO/-OH molar ratio change,the percentage content - COOH in the polymer,as well as the properties of waterborne polyurethane adhesive latex were studied。 

Keywords：waterborne polyurethane, dihydroxy methyl propionic acid, polymers,

adhesive

目   录

1  前言 4

2  实验部分 7

2。1  实验试剂 7

2。2  实验仪器 7

2。3  实验原理 7

2。3。1  WPU制备基本原理 7

2。3。2  水性聚氨酯胶黏剂合成路线 7

2。4  实验步骤 8

2。4。1  聚氨酯胶黏剂乳液的制备 8

2。4。2  胶膜的制备 8

2．5  测试与表征 8

2。5。1  傅立叶红外光谱表征 8

2。5。2  热失重测试 9

2。5。3  耐水性能测试 9

2。5。4  乳液固含量的测定 9

2。5。5  贮存稳定性的测定 9

3  结果与讨论 9

3。1  反应时间的影响 9

3。2  亲水基团-COOH含量对水性聚氨酯胶乳及胶膜性能的影响 10

3。3  TMP含量对水性聚氨酯胶乳及胶膜性能的影响 13

3。4  -NCO/-OH比对水性聚氨酯胶乳及胶膜性能的影响 13

结  论 15

参 考 文 献 16

致  谢 17

1  前言来自优I尔Y论S文C网WWw.YoueRw.com 加QQ7520~18766

当前，我国综合国力迅速发展，人民生活质量得到改善，各行各业对胶黏剂的需求也随之增长。自第二次世界大战德国科学家拜耳与其同事们最早合成出聚氨酯材料后，聚氨酯材料便作为一种多功能高分子材料发展速度迅猛。聚氨酯因其良好的性能，极易加工成型，故而广泛用作于涂料、泡沫塑料、灌封胶、粘合剂等多方面领域。其原料来源广泛，综合性能优异，产品可直接由液体原料加工成型，并且通过调整配方，可在一个较宽的范围改变其力学性质，近年来得到充分的认可，几乎遍及交通运输、建筑、机械、家具、电子设备、印刷、冶矿等众多的领域[1-3]。