摘 要:将凹凸棒石-g-聚氮异丙基丙烯酰胺(PGS-g-PNIPAAM)与聚偏氟乙烯(PVDF)共混制备温敏性混合基质超滤膜,利用凝固浴温度诱导表面偏析增强超滤膜的亲水性改性。结果表明,在5 °C和20 °C下制备的混合基质膜膜面的含N1s量分别为1。77%和1。02%,而40 °C下制备的膜只有0。73%;5 °C和20 °C下制备的PVDF/PGS-g-PNIPAAM混合基质膜的初始水接触角分别为75。2°和75°,比40 °C制备的膜低大约6°;5 °C下制备的混合基质膜在40 °C时的纯水通量高达366 L·m-2·h-1,而40 °C下制备的膜仅达274 L·m-2·h-1,并且低温制备的混合基质膜的最大孔径小,膜厚度低,孔隙率大;过滤BSA溶液时,添加改性剂的PVDF膜渗透通量高,下降速率减慢;综上所述,温度诱导表面偏析增强了混合基质超滤膜的亲水性、渗透性以及抗污染性能。93806

毕业论文关 键 词:共混改性,表面偏析,聚偏氟乙烯,凹凸棒石,聚氮异丙基丙烯酰胺

Abstract: In this study, a thermo-responsive inorganic-organic nanofiber, palygorskite-g-poly(N-isopropylacrylamide) (PGS-g-PNIPAAM), was incorporated into PVDF matrix for hydrophilic modification。 We utilized surface segregation induced by controlled coagulation bath temperature (CBT) to acquire more hydrophilic membrane surface。 Through controlling the CBT, series membranes were fabricated and the hydrophilicity, permeation as well as microstructure were investigated。 The N1s contents of the hybrid ultrafiltration membranes prepared at 5 and 20 °C are 1。77% and 1。02%, respectively while the one of membrane prepared at 40 °C is just 0。73%。These resulted in higher hydrophilicity and permeability as well as thermo-responsiveness for membranes prepared at lower temperatures。 The initial water contact angle of PVDF/palygorskite-g-PNIPAAM hybrid ultrafiltration membrane prepared at 5 and 20 °C is 75。2° and 75°, respectively, which is about 6° lower than the one prepared at 40 °C。 A higher pure water flux (PWF) of about 366 L·m-2·h-1 at 40 °C was obtained for the hybrid membrane prepared at 5 °C while the one prepared at 40 °C only reached 274 L·m-2·h-1。 Meanwhile, membranes prepared at low temperature exhibited fewer macrovoids, lower membrane thickness and larger elongation。 During the filtration of BSA solution, the permeate fluxes of the modified PVDF membranes were much higher and declined more slowly than that of the pristine one。 Overall, the PNIPAAM modified PGS nanofiber is a promising additive for polymer matrix membranes to reduce fouling。 

Keywords: blending modification, surface segregation, polyvinylidene fluoride, palygorskite, poly(N-isopropylacrylamide)

目  录

1 引言 4

1。1 PVDF超滤膜的制备 4

1。2 PVDF超滤膜的亲水性改性 6

1。3 智能膜 8

1。4 立题意义和研究内容 8

2 实验部分 9

2。1 实验药品及仪器 9

2。2 温敏性聚偏氟乙烯-凹土棒石混合基质超滤膜的制备 10

2。3 膜的表面红外测试 11

2。4 膜表面XPS测试 11

2。5 膜的渗透性 11

2。6 膜孔径测试 12

2。7 膜的抗污染性能测试 12

3  实验结果与分析

上一篇:基于钾掺杂碳纳米管的高灵敏性胆固醇生物传感器的研究
下一篇:没有了

温敏性聚偏氟乙烯-凹凸棒...

杀菌性水性聚氨酯胶粘剂的合成及应用

温敏性聚偏氟乙烯-凹凸棒...

预聚体分散水性聚氨酯胶黏剂的制备

温敏性凹土/聚偏氟乙烯复...

水性聚氨酯胶黏剂的制备

碳化硅改性水性聚氨酯的研究

跨国企业在华并购对我国企业的影响

扁平化设计在移动终端界面设计中的应用

我国乡村义务教育的困境与出路

区域产业与职业教育相互渗透探析【3057字】

国家法律哪个规定14岁是妇女

湖南省再婚生育新政策,...

功率分配器研究现状和发展趋势

英汉翻译中的模糊语现象浅析

高校就业困难毕业生群体...

對游戏用于中班幼儿美术教育探讨【2146字】