摘要本文研究了钾中毒对MnOx-CeO2催化剂NH3-SCR反应的影响。实验结果显示钾中毒会降低MnOx-CeO2催化剂的SCR反应活性，采用程序升温脱附、瞬态反应、原位红外和稳态动力学等方法对其反应机理进行研究。程序升温脱附结果表明MnOx-CeO2催化剂钾中毒会抑制NH3和NO的吸附。原位红外和瞬态反应结果进一步表明，MnOx-CeO2催化剂钾中毒会减少催化剂表面NH3的吸附量并改变催化剂表面吸附的硝酸盐物种，从而抑制经Eley-Rideal机理生成N2O，促进经Langmuir-Hinshelwood机理生成N2O。稳态动力学研究表明，MnOx-CeO2催化剂钾中毒会降低通过Langmuir-Hinshelwood机理和Eley-Rideal机理还原NO的速率，抑制NSCR反应，同时促进C-O反应。30724
- 上一篇：Mn/FeTi尖晶石对燃煤烟气中零价汞的脱除
- 下一篇：NiO-Ni(OH)2复合物的合成及其性能研究
关键词 NH3-SCR MnOx-CeO2催化剂 钾中毒 稳态动力学
毕业论文设计说明书外文摘要
Title Effect of Potassium Poisoning of a Mn-Ce Catalyst for the Selective Catalytic Reduction of NOx with NH3
Abstract
The effect of potassium poisoning of a MnOx-CeO2 catalyst for the selective catalytic reduction of NOx with NH3 (NH3-SCR) was investigated in this work. The experimental results showed that the SCR performance over MnOx-CeO2 catalyst decreased after the catalyst poisoned by potassium. And then the reaction mechanism was studied using temperature programmed desorption (TPD), transient reaction, in situ diffuse reflectance infrared Fourier transform spectra (in situ DRIFTS), steady-state kinetic study and so on. The TPD result indicated that the adsorption activities of NH3 and NO over MnOx-CeO2 catalyst were restrained due to potassium poisoning. The in situ DRIFTS and transient reaction results further suggested that the adsorption quantity of NH3 on catalyst surface decreased and the nitrate species adsorbed on catalyst surface changed after the potassium deposited on MnOx-CeO2 catalyst. Therefore, the formation of N2O through Eley-Rideal mechanism was restrained and the formation of N2O through Langmuir-Hinshelwood mechanism was promoted. In addition, the steady-state kinetic study indicated that the rate of NO reduction through Langmuir-Hinshelwood mechanism and Eley-Rideal mechanism decreased, the NSCR reaction was restrained and the C-O reaction was promoted in the meantime after the MnOx-CeO2 catalyst poisoned by potassium.
Keywords NH3-SCR MnOx-CeO2 catalyst potassium poisoning steady-state reaction kinetic
目 次
1 引言 1
1.1 氮氧化物的来源及危害 1
1.2 烟气脱硝技术 1
1.3 研究意义及主要内容 4
2 实验部分 6
2.1 实验仪器与试剂 6
2.2 催化剂的制备 6
2.3 催化剂活性评价 7
2.4 催化剂表征 8
2.5 原位红外和瞬态反应 8
2.6 反应动力学 8
3 实验结果 10
3.1 催化剂活性评价 10
3.2 催化剂表征 10
3.3 原位红外与瞬态反应 14
3.4 稳态动力学 18
4 结果讨论 21
4.1 反应机理 21
4.2 动力学研究 22
4.3 模型验证 24
结 论 26
致 谢 27
参考文献28
1 引言
1.1 氮氧化物的来源及危害
氮氧化物（NOx）主要有NO、NO2、N2O、N2O3、N2O4和N2O5，其来源主要分为自然污染源和人为污染源，其中来自自然环境中的闪电、微生物作用等自然污染源的NOx生成量约为每年5×108 t，来自生产活动、机动车排气等人为污染源的NOx生成量约为每年5×107 t[1]。人为产生的NOx大部分来自燃料高温燃烧（90%以上），其次是来自化工生产中的有关过程，如硝酸生产、金属表面硝酸处理和硝化过程等。燃料燃烧产生的NOx分为燃料型、热力型和瞬时型[2]。因燃烧产生的NOx中NO占95%以上，其余主要是NO2。在大气环境中NO经过反应最终转化为NO2，因此NOx主要以NO、NO2的形式存在于大气中。
-
不同温度生物炭对重金属...
-
天然沸石对水中磷酸根离子吸附研究
-
紫外光吸收剂对沥青涂料耐老化性能的影响
-
OA油酸对K2SiF6:Mn4+形貌及发光性能影响研究
-
油酸对K2SiF6:Mn4+形貌及发光性能影响研究
-
冶金粉尘对铜离子的吸附性能研究
-
蜂窝状催化剂对脱硝性能的影响
C++最短路径算法研究和程序设计
巴金《激流三部曲》高觉新的悲剧命运
NFC协议物理层的软件实现+文献综述
上市公司股权结构对经营绩效的影响研究
浅析中国古代宗法制度
g-C3N4光催化剂的制备和光催化性能研究
江苏省某高中学生体质现状的调查研究
现代简约美式风格在室内家装中的运用
高警觉工作人群的元情绪...
中国传统元素在游戏角色...